Long-term operation of a heterogeneously catalyzed gas phase partial oxidation of propene to acrylic acid

ABSTRACT

A process for the long-term operation of a two-stage heterogeneously catalyzed gas phase partial oxidation of propene to acrylic acid, in which the temperature of the fixed catalyst beds is increased over the time and the gas phase partial oxidation is interrupted from time to time and an oxygen-containing gas mixture is conducted through the fixed catalyst beds at elevated temperature of the fixed catalyst beds.

This application is a 119(e) application of provisional application 60/515,659, filed Oct. 31, 2003.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a process for the long-term operation of a heterogeneously catalyzed gas phase partial oxidation of propene to acrylic acid, by initially conducting a starting reaction gas mixture 1 which comprises propene, molecular oxygen and at least one inert gas and contains the molecular oxygen and the propene in a molar O₂:C₃H₆ ratio of ≧1, in a first reaction stage, at elevated temperature, over a first fixed catalyst bed 1 whose catalysts are such that their active composition is at least one multimetal oxide containing molybdenum and/or tungsten and also at least one of the elements bismuth, tellurium, antimony, tin and copper, in such a way that the propene conversion in single pass is ≧93 mol % and the accompanying selectivity of acrolein formation and of acrylic acid by-production taken together are ≧90 mol %, optionally reducing the temperature of the product gas mixture 1 leaving the first reaction stage by direct and/or indirect cooling and optionally adding molecular oxygen and/or inert gas to the product gas mixture 1, and then conducting the product gas mixture 1, as a starting reaction gas mixture 2 which comprises acrolein, molecular oxygen and at least one inert gas and contains the molecular oxygen and the acrolein in a molar O₂:C₃H₄O ratio of ≧0.5, in a second reaction stage, at elevated temperature, over a second fixed catalyst bed 2 whose catalysts are such that their active composition is at least one multimetal oxide containing the elements molybdenum and vanadium, in such a way that the acrolein conversion in single pass is ≧90 mol % and the selectivity of acrylic acid formation assessed over both reaction stages, based on propene converted, is ≧80 mol %, and by, in order to counteract the deactivation both of the fixed catalyst bed 1 and of the fixed catalyst bed 2, independently increasing the temperature of the particular fixed catalyst bed over time.

2. Description of the Background

Acrylic acid is an important monomer which finds use as such or in the form of its alkyl esters for obtaining polymers which are suitable, for example, as adhesives.

It is known that acrylic acid can be prepared by two-stage heterogeneously catalyzed gas phase partial oxidation of propene to acrylic acid in a fixed catalyst bed (cf., for example, EP-A 1159247, DE-A 10313208, DE-A 19948248, EP-A 990636, EP-A 1106598, DE-A 3002829). In the first reaction stage, propene is substantially partially oxidized to acrolein and, in the second reaction stage, the acrolein formed in the first reaction stage is substantially partially oxidized to acrylic acid. It is significant that the industrial embodiment is normally configured in such a way that the acrolein formed in the first reaction stage is not removed, but rather conducted into the second reaction stage as a constituent of the product gas mixture leaving the first reaction stage, optionally supplemented by molecular oxygen and inert gas, and optionally cooled by direct and/or indirect cooling. The fixed catalyst bed used in the particular reaction stage is tailored to the particular reaction stage and different to the fixed catalyst bed used for the other reaction stage. In addition, the two reaction stages are heated independently in such a way that the particular fixed catalyst bed is at its optimum working temperature.

The particular features of the two reaction stages are known per se (cf., for example, EP-A 714 700, EP-A 700 893, EP-A 279 374, EP-A 575 897, etc.).

It is also known that such a two-stage process for heterogeneously catalyzed gas phase partial oxidation of propene to acrylic acid may be operated substantially continuously over prolonged periods over one and the same fixed catalyst beds. However, the fixed catalyst beds lose quality in the course of the operating time. In general, both their activity and the selectivity of the particular target product formation deteriorate in both stages.

In order, despite this, to operate the fixed catalyst beds, whose manufacture and exchange is comparatively inconvenient and costly, for as long as possible in a reactor system charged with them, the prior art attempts in highly differing ways to counteract their aging process.

EP-A 990 636 (for example page 8, lines 13 to 15), EP-A 1070700 (for example page 4, lines 49, 50) and EP-A 1 106 598 (for example page 13, lines 43 to 45) propose the substantial compensation of the reduction in the quality of the particular fixed catalyst bed by gradually increasing the temperature of the particular fixed catalyst bed in the course of the operating time under otherwise substantially constant operating conditions, in order to substantially retain the propene or acrolein conversion in single pass of the reaction gas mixture through the fixed catalyst beds.

In this context, the temperature of the fixed catalyst bed refers to the temperature of the fixed catalyst bed when the partial oxidation process is performed, except in the theoretical absence of a chemical reaction (i.e. without the influence of the heat of reaction). This also applies in this document. In contrast, effective temperature of the particular fixed catalyst bed refers in this document to the actual temperature of the fixed catalyst bed taking into account the heat of reaction of the partial oxidation. When the temperature of a fixed catalyst bed is not constant along the fixed catalyst bed (for example in the case of a plurality of temperature zones), the term temperature of the fixed catalyst bed in this document means the (numerical) average of the temperature along the fixed catalyst bed.

It is significant in the aforementioned context that the temperature of the reaction gas mixture (and thus also the effective temperature of a fixed catalyst bed) passes through a maximum value (known as the hotspot value) when it passes through a fixed catalyst bed. The difference between hotspot value and the temperature of the fixed catalyst bed at the location of the hotspot value is referred to as the hotspot expansion.

A disadvantage of the procedure recommended in EP-A 990 636 and in EP-A 1 106 598 is that, with increasing increase in the temperature of the fixed catalyst bed, its aging process is accelerated (for example certain movement processes within the active compositions of the catalysts which contribute to aging proceed more rapidly). This is in particular because hotspot expansion usually rises more steeply than the temperature of the fixed catalyst bed itself with an increase in the temperature of the fixed catalyst bed (cf., for example, page 12, lines 45 to 48 of EP-A 1 106 598 and page 8, lines 11 to 15 of EP-A 990 636). The effective temperature of the fixed catalyst bed therefore usually increases disproportionately in the hotspot region, which additionally promotes the aging of the fixed catalyst bed.

When a maximum value of the temperature of the fixed catalyst bed is attained, the fixed catalyst bed is therefore customarily fully exchanged.

However, a disadvantage of such a complete exchange is that it is comparatively costly and inconvenient. The process for preparing acrylic acid has to be interrupted for a prolonged time and the costs of catalyst preparation are likewise considerable.

Operating modes are therefore desired for processes for two-stage heterogeneously catalyzed gas phase partial oxidation of propene to acrylic acid which are helpful in further prolonging the on-stream time of the fixed catalyst beds in the reactor system.

In this regard, DE-A 102 32 748 recommends, instead of fully exchanging the fixed catalyst bed, only replacing a portion thereof with a fresh catalyst charge.

A disadvantage of this proposal is that even a partial change of the fixed catalyst bed is accompanied by significant cost and inconvenience.

EP-A 614 872, which relates in particular to the second reaction stage in which the acrolein is partially oxidized to acrylic acid, recommends extending the on-stream time of a second stage fixed catalyst bed by, after operating the fixed catalyst bed for several years, which is accompanied by increases in the temperature thereof of from 15° C. to 30° C. and more, interrupting the process for partial oxidation, and, at fixed catalyst bed temperatures of from 260 to 450° C., conducting a gas mixture composed of oxygen, steam and inert gas through it, and subsequently continuing the partial oxidation.

In this context, inert gases in a gas mixture which is conducted through a fixed catalyst bed under certain conditions refers in this document to those gases of which at least 95 mol %, preferably at least 98 mol %, most preferably at least 99 mol % or 99.5 mol %, remain unchanged when they are conducted through the fixed catalyst bed. Regarding the gas mixture G to be used in accordance with the invention, steam should not be included under the term inert gas.

EP-A 169 449, which relates substantially to the first reaction stage in which the propene is partially oxidized to acrolein, recommends extending the on-stream time of the fixed catalyst bed by, after operating the fixed catalyst bed for several years, which is accompanied by increases in the temperature thereof of 15° C. and more, interrupting the process for partial oxidation, and, at fixed catalyst bed temperatures of from 380 to 540° C., conducting a gas consisting substantially of air through it, and subsequently continuing the partial oxidation.

EP-A 339 119 recommends, with an analogous mode of operation, the use of a gas comprising oxygen and steam.

However, a disadvantage of the procedures of EP-A 339 119, EP-A 169 449 and of EP-A 614 872 is that, up to the point at which the partial oxidation is interrupted, the aging of the fixed catalyst bed continues and is promoted unhindered.

It is an object of the present invention to provide a process for long-term operation of a two-stage heterogeneously catalyzed gas phase partial oxidation of propene to acrylic acid, in which the catalyst aging is counteracted in both stages in a manner by which the intensity of the hotspot expansion in both stages over time is lower than in the prior art processes.

SUMMARY OF THE INVENTION

We have found that this object is achieved by a process for the long-term operation of a heterogeneously catalyzed gas phase partial oxidation of propene to acrylic acid, by initially conducting a starting reaction gas mixture 1 which comprises propene, molecular oxygen and at least one inert gas and contains the molecular oxygen and the propene in a molar O₂:C₃H₆ ratio of ≧1, in a first reaction stage, at elevated temperature, over a first fixed catalyst bed 1 whose catalysts are such that their active composition is at least one multimetal oxide containing molybdenum and/or tungsten and also at least one of the elements bismuth, tellurium, antimony, tin and copper, in such a way that the propene conversion in single pass is ≧93 mol % and the accompanying selectivity of acrolein formation and of acrylic acid by-production taken together are ≧90 mol % (preferably ≧92 mol %, or ≧94 mol %, or ≧96 mol %, or ≧98 mol %), optionally reducing the temperature of the product gas mixture 1 leaving the first reaction stage by direct and/or indirect cooling and optionally adding molecular oxygen and/or inert gas to the product gas mixture 1, and then conducting the product gas mixture 1, as a starting reaction gas mixture 2 which comprises acrolein, molecular oxygen and at least one inert gas and contains the molecular oxygen and the acrolein in a molar O₂:C₃H₄O ratio of ≧0.5, in a second reaction stage, at elevated temperature, over a second fixed catalyst bed 2 whose catalysts are such that their active composition is at least one multimetal oxide containing the elements molybdenum and vanadium, in such a way that the acrolein conversion in single pass is ≧90 mol % and the selectivity of acrylic acid formation assessed over both reaction stages, based on propene converted, is ≧80 mol % (preferably ≧83 mol %, or ≧85 mol %, or ≧88 mol %, or 90 mol %, or ≧93 mol %), and by, in order to counteract the deactivation both of the fixed catalyst bed 1 and of the fixed catalyst bed 2, independently increasing the temperature of the particular fixed catalyst bed over time, which comprises interrupting the gas phase partial oxidation at least once before the temperature increase of the fixed catalyst bed 2 is permanently ≧10° C., and, at a temperature of the fixed catalyst bed 1 of from 250 to 550° C. and a temperature of the fixed catalyst bed 2 of from 200 to 450° C. initially conducting a gas mixture G consisting of molecular oxygen, inert gas and optionally steam through the fixed catalyst bed 1, and subsequently optionally through an intermediate cooler and finally through the fixed catalyst bed 2.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic diagram of a rotary tube furnace used for calcination in the preparation of starting compositions 1 and 2.

FIG. 2 is a graph showing the percentage of M^(A) as a function of material temperature in ° C.

FIG. 3 is a graph showing ammonia concentration of atmosphere A in percent by volume over thermal treatment as a function of material temperature in ° C.

DETAILED DESCRIPTION OF THE INVENTION

It is surprising that, when the process according to the invention is employed, long-term operation of a two-stage heterogeneously catalyzed gas phase partial oxidation of propene to acrylic acid is possible, by which the intensity of the hotspot expansion over time is lower than in the prior art processes. In favorable cases, the intensities of the hotspot expansion over time remain constant or even decrease. In addition, the selectivity of the particular target product formation remains substantially constant over time and in favorable cases even increases.

According to the invention, the gas phase partial oxidation will preferably be interrupted at least once even before the temperature increase of the fixed catalyst bed 2 is permanently ≧8° C., or ≧7° C., or ≧6° C., or ≧5° C., or ≧4° C., in order to conduct the gas mixture G through the fixed catalyst beds in the inventive manner.

Particular preference is given in the process according to the invention to interrupting the gas phase partial oxidation at least once even before the temperature increase of the fixed catalyst bed 2 is permanently ≧3° C. or ≧2° C., in order to conduct the gas mixture G through the fixed catalyst beds in the inventive manner.

However, the process according to the invention is also advantageous when, before the temperature increase of the fixed catalyst bed 2 is permanently ≧1° C. or less, the gas phase partial oxidation is interrupted at least once and the gas mixture G is conducted through the fixed catalyst beds in the inventive manner.

However, the temperature increase of the fixed catalyst bed 2 will generally be permanently ≧0.1° C. or ≧0.2° C. before the gas phase partial oxidation of propene to acrylic acid is interrupted at least once in accordance with the invention.

The phrase “before the implemented temperature increase of the fixed catalyst bed 2 is permanently ≧10° C. or ≧8° C. (generally ≧X° C.)” takes into account that the temperature of a fixed catalyst bed 2 on the industrial scale may undergo certain deviations for various reasons. In this case, the actual profile of the temperature of the fixed catalyst bed 2 is plotted over time and a fitted curve is drawn through the measurement points by the deviation of least squares method developed by Legendre and Gauss. When a temperature increase of ≧10° C. or ≧8° C. (generally of ≧X° C.) is achieved on this fitted curve, the feature “permanent” is fulfilled.

Advantageously in accordance with the invention, the temperature of the fixed catalyst bed 1 when gas mixture G is passed through in accordance with the invention is from 300 to 500° C., more preferably from 300 to 400° C., most preferably from 300 to 360° C.

The temperature of the fixed catalyst bed 2 when gas mixture G is passed through in accordance with the invention is preferably from 250 to 400° C., often from 250 to 350° C. and in many cases from 250 to 300° C.

Favorably in accordance with the invention, the temperature of the fixed catalyst bed 1, while the gas mixture G is conducted through in the course of the implementation of the process according to the invention, is kept at a value T_(G1) which corresponds substantially to that temperature T_(V1) of the fixed catalyst bed 1 which it had in the course of operation of the partial oxidation before it was interrupted in order to conduct the gas mixture G through the fixed catalyst bed 1 in accordance with the invention.

In other words, advantageously in accordance with the invention, T_(G1)=T_(V1)±50° C., or T_(G1)=T_(V1)±20° C., and very particularly advantageously, T_(G1)=T_(V1). Normally, T_(V1) will be in the range from 250 to 450° C., frequently in the range from 300 to 400° C.

The temperature of the fixed catalyst bed 2 while the gas mixture G is conducted through in accordance with the invention will preferably be kept at a value T_(G2) which corresponds substantially to that temperature T_(V2) of the fixed catalyst bed 2 that the fixed catalyst bed 2 had during the operation of the partial oxidation before it was interrupted for the purpose of conducting the gas mixture G through in accordance with the invention.

In other words, advantageously in accordance with the invention, T_(G2)=T_(V2)±50° C., or T_(G2)=T_(V2)±20° C., and, very particularly advantageously, T_(G2)=T_(V2). Normally, T_(V2) will be in the range from 200 to 400° C., frequently in the range from 220 to 350° C.

The duration t_(G) over which the gas mixture G is to be conducted through the catalyst beds in the process according to the invention will generally be less that 2 h, frequently from 6 h to 120 h, in many cases from 12 h to 72 h and often from 20 h to 40 h. However, it may also be 10 days and more. In general, a smaller oxygen content of the gas mixture G will result in a longer duration t_(G). Increased oxygen contents in the gas mixture G are advantageous according to the invention.

Typically, the duration t_(G) will at least be sufficiently long that the oxygen content of the gas mixture G when it leaves the fixed catalyst bed 2 will no longer differ from the oxygen content of the gas mixture G when it enters the fixed catalyst bed 1.

Between fixed catalyst beds 1 and 2, supplementation with fresh gas mixture G may optionally be effected in the process according to the invention. However, preference is given to not carrying out such a supplementation in the process according to the invention.

In general, the gas mixture G will be conducted through the fixed catalyst beds in accordance with the invention in the process according to the invention at a frequency F of at least once per calendar year, preferably of at least once every three-quarter calendar year or every half calendar year, more preferably at least once every calendar quarter and more preferably at least once per calender month.

In other words, the gas mixture G will be conducted through the fixed catalyst beds in accordance with the invention in the process according to the invention at least once within 7 500 or 7 000, or 6 000, preferably at least once within 5 500 or 5 000, and most preferably at least once within 4 000, or 3 000, or 2 000, or 1500, or 1000, or 500, operating hours of the partial oxidation. Frequent performance of the process according to the invention has an advantageous effect.

Otherwise the process for heterogeneously catalyzed gas phase partial oxidation of propene to acrylic acid will be carried out substantially continuously.

Frequently, the increase in the temperature of the fixed catalyst bed 1 will be carried out in the process according to the invention in such a way that the propene conversion in single pass of the reaction gas mixture through the fixed catalyst bed 1 does not go below 93 mol %, or 94 mol %, or 95 mol %, or 96 mol %, or 97 mol %.

In other words, the temperature of the fixed catalyst bed 1 will normally be increased at least once before 7 500 or 7 000, usually before 6 000, and in many cases before 5 000, or 4 000, or 3 000, operating hours of the partial oxidation have been attained.

In a particularly appropriate manner, the increase in the temperature of the fixed catalyst bed 1 in the process according to the invention will preferably be carried out using particularly favorable catalysts (for example those recommended in this document) (usually substantially continuously and) in such a way that the propene content in the product gas mixture of the first reaction stage does not exceed the value 10 000 ppm by weight, preferably 6 000 ppm by weight and more preferably 4 000 or 2 000 ppm by weight.

In addition, the residual oxygen in the product gas mixture of the first reaction stage should be at least 1% by volume, preferably at least 2% by volume and more preferably at least 3% by volume.

The increase in the temperature of the fixed catalyst bed 2 in the process according to the invention will similarly appropriately be carried out in such a way that the acrolein conversion in single pass of the reaction gas mixture through the fixed catalyst bed 2 does not go below 90 mol %, or 92 mol %, or 93 mol %, or 94 mol %, or 96 mol %, or 98 mol %, or 99 mol %.

In other words, the temperature of the fixed catalyst bed 2 will normally be increased at least once before 7 500 or before 7 000, usually before 6 000 and in many cases before 5 000, or 4 000 or 3 000, operating hours of the partial oxidation have been attained.

In a particularly appropriate manner, the increase in the temperature of the fixed catalyst bed 2 in the process according to the invention will preferably be carried out using particularly favorable catalysts (for example those recommended in this document or in JP-A 7-10802) (usually substantially continuously and) in such a way that the acrolein content in the product gas mixture of the first reaction stage does not exceed the value 1 500 ppm by weight, preferably 600 ppm by weight and more preferably 350 ppm by weight. This takes into account that acrolein has a disruptive influence on the partial oxidation in the process of removing acrylic acid from the product gas mixture in that it promotes the polymerization tendency of acrylic acid (cf. EP-A 1 041 062).

In addition, the residual oxygen in the product gas mixture of the second reaction stage should be at least 1% by volume, preferably at least 2% by volume and more preferably at least 3% by volume.

Appropriately from an application point of view, the gas mixture G in the process according to the invention will contain at least 1% by volume or 2% by volume, preferably at least 3% by volume and more preferably at least 4% by volume, of oxygen. However the oxygen content of the gas mixture G will generally be ≦21% by volume. In other words, a possible gas mixture G is air. Another possible gas mixture G is lean air. This is air depleted of oxygen.

Advantageous in accordance with the invention is lean air which consists of from 3 to 10% by volume, preferably from 4 to 6% by volume of oxygen, and a remainder of molecular nitrogen. Appropriately in accordance with the invention, the gas mixture G contains substantially no steam. However, the gas mixture G to be used in accordance with the invention may contain up to 0.1% by volume, or up to 0.5% by volume, or up to 1% by volume, of steam. Normally, the steam content of the gas mixture G is generally ≦75% by volume. The inert gas content of the gas mixture G is generally ≦95% by volume, usually ≦90% by volume.

Gas mixtures G which are suitable in accordance with the invention may thus consist, for example, of from 3 to 20% by volume, preferably from 4 to 6% by volume, of oxygen, from 0 to 5% by volume of steam and a remainder of inert gas. Preferred inert gases are N₂ and CO₂. Useful gas mixtures G for the process according to the invention are in particular all of those recommended in EP-A 339 119, in EP-A 169 449 and in EP-A 614 872. All regeneration conditions recommended in these documents may likewise be employed for the process according to the invention.

The amount of the gas mixture G conducted through the fixed catalyst bed 1 in the process according to the invention may be from 5 or 100 to 5 000 l (STP)/l·h, preferably from 20 or 200 to 3 000 l (STP)/l·h. The reference basis is the volume of the overall fixed catalyst bed 1, i.e. including any sections used which consist exclusively of inert material. High hourly space velocities of gas mixture G have been found to be advantageous in accordance with the invention.

Suitable multimetal oxide compositions for the catalysts of the first reaction stage of the process according to the invention:are in particular active multimetal oxides comprising Mo, Bi and Fe. These are in particular the multimetal oxide compositions comprising Mo, Bi and Fe disclosed in DE-A 103 44 149 and DE-A 103 44 264.

These are in particular also the multimetal oxide active compositions of the general formula I of DE-A 199 55 176, the multimetal oxide active compositions of the general formula I of DE-A 199 48 523, the multimetal oxide active compositions of the general formulae I, II and III of DE-A 10101695, the multimetal oxide active compositions of the general formulae I, II and III of DE-A 19948248 and the multimetal oxide active compositions of the general formulae I, II and III of DE-A 19955168 and also the multimetal oxide active compositions specified in EP-A 700714.

Also suitable for the fixed catalyst bed 1 to be used according to the invention are the multimetal oxide catalysts comprising Mo, Bi and Fe which are disclosed in the documents DE-A 10046957, DE-A 10063162, DE-C 3338380, DE-A 19902562, EP-A 15565, DE-C 2380765, EP-A 807465, EP-A 279374, DE-A 3300044, EP-A 575897, U.S. Pat. No. 4,438,217, DE-A 19855913, WO 98/24746, DE-A 19746210 (those of the general formula 11), JP-A 91/294239, EP-A 293224 and EP-A 700714. This applies in particular to the exemplary embodiments in these documents, and among these particular preference is given to those of EP-A 15565, EP-A 575897, DE-A 19746210 and DE-A 19855913. Particular emphasis is given in this context to a catalyst according to example 1c from EP-A 15565 and also to a catalyst to be prepared in a corresponding manner but whose active composition has the composition Mo₁₂Ni_(6.5)Zn₂Fe₂Bi₁P_(0.0065)K_(0.06)Ox·10 SiO₂. Emphasis is also given to the example having the serial number 3 from DE-A 19855913 (stoichiometry: Mo₁₂Co₇Fe₃Bi_(0.6)K_(0.08)Si_(1.6)Ox) as an unsupported hollow cylinder catalyst of geometry 5 mm×3 mm×2 mm or 5 mm×2 mm×2 mm (each external diameter×height×internal diameter) and also to the unsupported multimetal oxide 11 catalyst according to example 1 of DE-A 19746210. Mention should also be made of the multimetal oxide catalysts of U.S. Pat. No. 4,438,217. The latter is true in particular when these have a hollow cylinder geometry of the dimensions 5.5 mm×3 mm×3.5 mm, or 5 mm×2 mm×2 mm, or 5 mm×3 mm×2 mm, or 6 mm×3 mm×3 mm, or 7 mm×3 mm×4 mm (each external diameter×height×internal diameter). Likewise suitable are the multimetal oxide catalysts and geometries of DE-A 10101695 or WO 02/062737.

Also suitable are example 1 of DE-A 10046957 (stoichiometry: [Bi₂W₂O₉×2WO₃]_(0.5)·[Mo₁₂Co_(5.6)Fe_(2.94)Si_(1.59)K_(0.08)O_(x)]₁) as an unsupported hollow cylinder (ring) catalyst of geometry 5 mm×3 mm×2 mm or 5 mm×2 mm×2 mm (each external diameter×length×internal diameter), and also the coated catalysts 1, 2 and 3 of DE-A 10063162 (stoichiometry: Mo₁₂Bi_(1.0)Fe₃Co₇Si_(1.6)K_(0.08)), except as annular coated catalysts of appropriate coating thickness and applied to support rings of geometry 5 mm×3 mm×1.5 mm or 7 mm×3 mm×1.5 mm (each external diameter×length×internal diameter).

A multitude of the multimetal oxide active compositions suitable for the catalysts of the fixed catalyst bed 1 required for the process according to the invention can be encompassed by the general formula I Mo₁₂Bi_(a)Fe_(b)X¹ _(c)X² _(d)X³ _(e)X⁴ _(f)O_(n)  (I) in which the variables are defined as follows:

-   X¹=nickel and/or cobalt, -   X²=thallium, an alkali metal and/or an alkaline earth metal, -   X³=zinc, phosphorus, arsenic, boron, antimony, tin, cerium, lead     and/or tungsten, -   X⁴=silicon, aluminum, titanium and/or zirconium, -   a=from 0.5to 5, -   b=from 0.01 to 5, preferably from 2 to 4, -   c=from 0 to 10, preferably from 3 to 10, -   d=from 0 to 2, preferably from 0.02 to 2, -   e=from 0 to 8, preferably from 0 to 5, -   f=from 0 to 10 and -   n=a number which is determined by the valency and frequency of the     elements in I other than oxygen.

They are obtainable in a manner known per se (see, for example, DE-A 4023239) and are customarily shaped undiluted to give spheres, rings or cylinders or else used in the form of coated catalysts, i.e. preshaped inert support bodies coated with the active composition. It will be appreciated that they may also be used as catalysts in powder form.

In principle, active compositions of the general formula I can be prepared in a simple manner by obtaining a very intimate, preferably finely divided dry mixture corresponding to their stoichiometry from suitable sources of their elemental constituents and calcining it at temperatures of from 350 to 650° C. The calcination may be effected either under inert gas or under an oxidative atmosphere, for example air (mixture of inert gas and oxygen) and also under a reducing atmosphere (for example mixture of inert gas, NH₃, CO and/or H₂). The calcination time can be from a few minutes to a few hours and typically decreases with temperature. Useful sources for the elemental constituents of the multimetal oxide active compositions I are those compounds which are already oxides and/or those compounds which can be converted to oxides by heating, at least in the presence of oxygen.

In addition to the oxides, such useful starting compounds include in particular halides, nitrates, formates, oxalates, citrates, acetates, carbonates, amine complexes, ammonium salts and/or hydroxides (compounds such as NH₄OH, (NH₄)₂CO₃, NH₄NO₃, NH₄CHO₂, CH₃COOH, NH₄CH₃CO₂ and/or ammonium oxalate which decompose and/or can be decomposed on later calcining at the latest to give compounds which are relased in gaseous form can be additionally incorporated into the intimate dry mixture).

The starting compounds for preparing the multimetal oxide active compositions I can be intimately mixed in dry or in wet form. When they are mixed in dry form, the starting compounds are advantageously used as finely divided powders and subjected to calcination after mixing and optional compacting. However, preference is given to intimate mixing in wet form. Customarily, the starting compounds are mixed with each other in the form of an aqueous solution and/or suspension. Particularly intimate dry mixtures are obtained in the mixing process described when the starting materials are exclusively sources of the elemental constituents in dissolved form. The solvent used is preferably water. Subsequently, the aqueous composition obtained is dried, and the drying process is preferably effected by spray-drying the aqueous mixture at exit temperatures from the spray tower of from 100 to 150° C.

Typically, the multimetal oxide active compositions of the general formula I are used in the fixed catalyst bed 1 required according to the invention not in powder form, but rather shaped into certain catalyst geometries, and the shaping may be effected either before or after the final calcination. For example, unsupported catalysts can be prepared from the powder form of the active composition or its uncalcined and/or partially calcined precursor composition by compacting to the desired catalyst geometry (for example by tableting or extruding), optionally with the addition of assistants, for example graphite or stearic acid as lubricants and/or shaping assistants and reinforcing agents such as microfibers of glass, asbestos, silicon carbide or potassium titanate. Examples of suitable unsupported catalyst geometries include solid cylinders or hollow cylinders having an external diameter and a length of from 2 to 10 mm. In the case of the hollow cylinder, a wall thickness of from 1 to 3 mm is advantageous. It will be appreciated that the unsupported catalyst can also have spherical geometry, and the spherical diameter can be from 2 to 10 mm.

A particularly advantageous hollow cylinder geometry is 5 mm×3 mm×2 mm (external diameter×length×internal diameter), in particular in the case of unsupported catalysts.

It will be appreciated that the pulverulent active composition or its pulverulent precursor composition which is yet to be calcined and/or partially calcined may also be shaped by applying to preshaped inert catalyst supports. The coating of the support bodies to produce the coated catalysts is generally performed in a suitable rotatable vessel, as disclosed, for example, by DE-A 2909671, EP-A 293859 or EP-A 714700. To coat the support bodies, the powder composition to be applied is advantageously moistened and dried again after application, for example by means of hot air. The coating thickness of the powder composition applied to the support body is advantageously selected within the range from 10 to 1 000 μm, preferably within the range from 50 to 500 μm and more preferably within the range from 150 to 250 μm.

Useful support materials are the customary porous or nonporous aluminum oxides, silicon dioxide, thorium dioxide, zirconium dioxide, silicon carbide or silicates such as magnesium silicate or aluminum silicate. They generally behave substantially inertly with regard to the target reaction on which the process according to the invention in the first reaction stage is based. The support bodies can have a regular or irregular shape, although preference is given to regularly shaped support bodies having distinct surface roughness, for example spheres or hollow cylinders. It is suitable to use substantially nonporous, surface-roughened spherical supports made of steatite (e.g. Steatite C220 from CeramTec) whose diameter is from 1 to 8 mm, preferably from 4 to 5 mm.

However, suitable support bodies also include cylinders whose length is from 2 to 10 mm and whose external diameter is from 4 to 10 mm. In the case of rings suitable as support bodies according to the invention, the wall thickness is also typically from 1 to 4 mm. According to the invention, annular support bodies to be used preferably have a length of from 2 to 6 mm, an external diameter of from 4 to 8 mm and a wall thickness of from 1 to 2 mm. Suitable as support bodies according to the invention are in particular rings of the geometry 7 mm×3 mm×4 mm or 5 mm×3 mm×2 mm (external diameter×length×internal diameter). It will be appreciated that the fineness of the catalytically active oxide compositions to be applied to the surface of the support body will be adapted to the desired coating thickness (cf. EP-A 714 700).

Suitable multimetal oxide active compositions for the catalysts of the fixed catalyst bed 1 of the process according to the invention are also compositions of the general formula II [Y¹ _(a′)Y² _(b′)O_(x′)]_(p)[Y³ _(c′)Y⁴ _(d′)Y⁵ _(e′)Y⁶ _(f′)Y⁷ _(g′)Y² _(h′)O_(y′)]_(q)  (II) in which the variables are defined as follows:

-   Y¹=only bismuth or bismuth and at least one of the elements     tellurium, antimony, tin and copper, -   Y²=molybdenum or molybdenum and tungsten, -   Y³=an alkali metal, thallium and/or samarium, -   Y⁴=an alkaline earth metal, nickel, cobalt, copper, manganese, zinc,     tin, cadmium and/or mercury, -   Y⁵=iron or iron and at least one of the elements chromium and     cerium, -   Y=phosphorus, arsenic, boron and/or antimony, -   Y⁷=a rare earth metal, titanium, zirconium, niobium, tantalum,     rhenium, ruthenium, rhodium, silver, gold, aluminum, gallium,     indium, silicon, germanium, lead, thorium and/or uranium, -   a′=from 0.01 to 8, -   b′=from 0.1 to 30, -   c′=from 0 to 4, -   d′=from 0 to 20, -   e′=from >0 to 20, -   f′=from 0 to 6, -   g′=from 0 to 15, -   h′=from 8 to 16, -   x′,y′=numbers which are determined by the valency and frequency of     the elements in II other than oxygen and -   p,q =numbers whose p/q ratio is from 0.1 to 10,     comprising three-dimensional regions of the chemical composition Y¹     _(1′)Y² _(b′)O_(x′) which are delimited from their local environment     as a consequence of their different chemical composition from their     local environment, and whose maximum diameter (longest line passing     through the center of the region and connecting two points on the     surface (interface)) is from 1 nm to 100 μm, frequently from 10 nm     to 500 nm or from 1 μm to 50 or 25 μm.

Particularly advantageous multimetal oxide compositions Y¹ are those in which Y¹ is only bismuth.

Among these, preference is given in turn to those of the general formula III [Bi_(a″)Z² _(b″)O_(x″)]_(p″) [Z² ₁₂Z³ _(c″)Z⁴ _(d″)Fe_(e″)Z⁵ _(f″)Z⁶ _(g″)Z⁷ _(h″)O_(y″)]_(q″)  (III) in which the variables are defined as follows:

-   Z²=molybdenum or molybdenum and tungsten, -   Z³=nickel and/or cobalt, -   Z⁴=thallium, an alkali metal and/or an alkaline earth metal, -   Z⁵=phosphorus, arsenic, boron, antimony, tin, cerium and/or lead, -   Z⁶=silicon, aluminum, titanium and/or zirconium, -   Z⁷=copper, silver and/or gold, -   a″=from 0.1 to 1, -   b″=from 0.2 to 2, -   c″=from 3 to 10, -   d″=from 0.02 to 2, -   e″=from 0.01 to 5, preferably from 0.1 to 3, -   f″=from 0 to 5, -   g″=from 0 to 10, -   h″=from 0 to 1, -   x″,y″=numbers which are determined by the valency and frequency of     the elements in III other than oxygen, -   p″,q″=numbers whose p″/q″ratio is from 0.1 to 5, preferably from 0.5     to 2,

and very particular preference is given to those compositions III in which Z² _(b″)=(tungsten)_(b″) and Z² ₁₂=(molybdenum)₁₂.

It is also advantageous when at least 25 mol % (preferably at least 50 mol % and more preferably at least 100 mol %) of the total proportion of [Y¹ _(a′)Y² _(b′)O_(x′)]_(p) ([Bi_(a″)Z² _(b″)O_(x″)]_(p″)) of the multimetal oxide compositions II (multimetal oxide compositions III) suitable according to the invention in the multimetal oxide compositions II (multimetal oxide compositions III) suitable according to the invention are in the form of three-dimensional regions of the chemical composition Y¹ _(a′)Y² _(b′)O_(x′) [Bi_(a″)Z² _(b″)O_(x″)] which are delimited from their local environment as a consequence of their different chemical composition from their local environment, and whose maximum diameter is in the range from 1 nm to 100 μm.

With regard to the shaping, the statements made for the multimetal oxide I catalysts apply to the multimetal oxide II catalysts.

The preparation of multimetal oxide active compositions i II s described, for example, in EP-A 575897 and also in DE-A 19855913, DE-A 10344149 and DE-A 10344264.

Suitable active compositions for the catalysts of the fixed catalyst bed 2 are, as is well known, multimetal oxides which comprise the elements Mo and V.

Multimetal oxide active compositions comprising Mo and V which are suitable in accordance with the invention may be taken, for example, from U.S. Pat. No. 3,775,474, U.S. Pat. No. 3,954,855, U.S. Pat. No. 3,893,951, and U.S. Pat. No. 4,339,355, or EP-A 614872 or EP-A 1041062, or WO 03/055835, or WO 03/057653.

Especially suitable are also the multimetal oxide active compositions of DE-A 10325487 and also of DE-A 10325488.

Also particularly suitable as active compositions for fixed bed 2 catalysts suitable for the process according to the invention are the multimetal oxide compositions of EP-A 427508, DE-A 2909671, DE-C 3151805, DE-B 2626887, DE-A 4302991, EP-A 700893, EP-A 714700 and DE-A 19736105. Particular preference is given in this context to the exemplary embodiments of EP-A 714 700 and of DE-A 19 73 6105.

A multitude of these multimetal oxide active compositions suitable for said fixed bed 2 catalysts can be encompassed by the general formula IV Mo₁₂V_(a)X¹ _(b)X² _(c)X³ _(d)X⁴ _(e)X₅ _(f)X⁶ _(g)O_(n)  (IV) in which the variables are defined as follows:

-   X¹=W, Nb, Ta, Cr and/or Ce, -   X²=Cu, Ni, Co, Fe, Mn and/or Zn, -   X³=Sb and/or Bi, -   X⁴=one or more alkali metals, -   X⁵=one or more alkaline earth metals, -   X⁶=Si, Al, Ti and/or Zr, -   a=from 1 to 6, -   b=from 0.2 to 4, -   c=from 0.5 to 18, -   d=from 0 to 40, -   e=from 0 to 2, -   f=from 0 to 4, -   g=from 0 to 40 and -   n=a number which is determined by the valency and frequency of the     elements in IV other than oxygen.

Preferred embodiments among the active multimetal oxides IV are those which are encompassed by the following definitions of the variables of the general formula IV:

-   X¹=W, Nb and/or Cr, -   X²=Cu, Ni, Co and/or Fe, -   X³=Sb, -   X⁴=Na and/or K, -   X⁵=Ca, Sr and/or Ba, -   X⁶=Si, Al and/or Ti, -   a=from 1.5 to 5, -   b=from 0.5 to 2, -   c=from 0.5 to 3, -   d=from 0 to 2, -   e=from 0 to 0.2, -   f=from 0 to 1 and -   n=a number which is determined by the valency and frequency of the     elements in IV other than oxygen.

However, multimetal oxides IV which are very particularly preferred according to the invention are those of the general formula V Mo₁₂V_(a′)Y¹ _(b′)Y² _(c′)Y⁵ _(f′)Y⁶ _(g′)O_(n′)  (V) where

-   Y¹=W and/or Nb, -   Y²=Cu and/or Ni, -   Y⁵=Ca and/or Sr, -   Y⁶=Si and/or Al, -   a′=from 2 to 4, -   b′=from 1 to 1.5, -   c′=from 1 to 3, -   f′=from 0 to 0.5 -   g′=from 0 to 8 and -   n′=a number which is determined by the valency and frequency of the     elements in V other than oxygen.

The multimetal oxide active compositions (IV) which are suitable according to the invention for catalysts of the fixed catalyst bed 2 are obtainable in a manner known per se, for example disclosed in DE-A 4335973 or in EP-A 714700. However, the multimetal oxide active compositions of DE-A 10 261 186 are also especially suitable.

In principle, suitable multimetal oxide active compositions for fixed bed 2 catalysts to be used for the process according to the invention, in particular those of the general formula IV can be prepared in a simple manner by obtaining a very intimate, preferably finely divided dry mixture having a composition corresponding to their stoichiometry from suitable sources of their elemental constituents and calcining it at temperatures of from 350 to 600° C. The calcination may be carried out either under inert gas or under an oxidative atmosphere, for example air (mixture of inert gas and oxygen), and also under a reducing atmosphere (for example mixtures of inert gas and reducing gases such as H₂, NH₃, CO, methane and/or acrolein or the reducing gases mentioned themselves). The calcination time can be from a few minutes to a few hours and typically decreases with temperature. Useful sources for the elemental constituents of the multimetal oxide active compositions IV include those compounds which are already oxides and/or those compounds which can be converted to oxides by heating, at least in the presence of oxygen.

The starting compounds for preparing multimetal oxide compositions IV can be intimately mixed in dry or in wet form. When they are mixed in dry form, the starting compounds are advantageously used as finely divided powder and subjected to calcining after mixing and optional compaction. However, preference is given to intimate mixing in wet form.

This is typically done by mixing the starting compounds in the form of an aqueous solution and/or suspension. Particularly intimate dry mixtures are obtained in the mixing process described when the starting materials are exclusively sources of the elemental constituents in dissolved form. The solvent used is preferably water. Subsequently, the aqueous composition obtained is dried, and the drying process is preferably effected by spray-drying the aqueous mixture at exit temperatures of from 100 to 150° C.

The suitable multimetal oxide active compositions for fixed bed 2 catalysts to be used for the process according to the invention, in particular those of the general formula IV, may be used for the process according to the invention either in powder form or shaped to certain catalyst geometries, and the shaping may be effected before or after the final calcination. For example, unsupported catalysts can be prepared from the powder form of the active composition or its uncalcined precursor composition by compacting to the desired catalyst geometry (for example by tableting or extruding), optionally with the addition of assistants, for example graphite or stearic acid as lubricants and/or shaping assistants and reinforcing agents such as microfibers of glass, asbestos, silicon carbide or potassium titanate. Examples of suitable unsupported catalyst geometries are solid cylinders or hollow cylinders having an external diameter and a length of from 2 to 10 mm. In the case of the hollow cylinder, a wall thickness of from 1 to 3 mm is advantageous. It will be appreciated that the unsupported catalyst may also have spherical geometry and the spherical diameter may be from 2 to 10 mm.

It will be appreciated that the pulverulent active composition or its pulverulent precursor composition which is yet to be calcined can also be shaped by applying to preshaped inert catalyst supports. The coating of the support bodies to prepare the coated catalysts is generally performed in a suitable rotatable vessel, as disclosed, for example, by DE-A 2909671, EP-A 293859 or from EP-A 714700.

To coat the support bodies, the powder composition to be applied is appropriately moistened and is dried again after application, for example by means of hot air. The coating thickness of the powder composition applied to the support body is advantageously selected within the range from 10 to 1 000 μm, preferably within the range from 50 to 500 μm and more preferably in the range from 150 to 250 μm.

Useful support materials are customary porous or nonporous aluminum oxides, silicon dioxide, thorium dioxide, zirconium dioxide, silicon carbide or silicates such as magnesium silicate or aluminum silicate. The support bodies may have a regular or irregular shape, although preference is given to regularly shaped support bodies having distinct surface roughness, for example spheres or hollow cylinders. It is suitable to use substantially nonporous, surface-roughened, spherical supports made of steatite whose diameter is from 1 to 8 mm, preferably from 4 to 5 mm. However, suitable support bodies also include cylinders whose length is from 2 to 10 mm and whose external diameter is from 4 to 10 mm. In the case of rings which are suitable according to the invention as support bodies, the wall thickness is also typically from 1 to 4 mm. Annular support bodies to be used with preference in accordance with the invention have a length of from 3 to 6 mm, an external diameter of from 4 to 8 mm and a wall thickness of from 1 to 2 mm. Suitable support bodies according to the invention are also in particular rings of geometry 7 mm×3 mm×4 mm (external diameter×length×internal diameter). It will be appreciated that the fineness of the catalytically active oxide compositions to be applied to the surface of the support body is adapted to the desired coating thickness (cf. EP-A 714 700).

Advantageous multimetal oxide active compositions to be used for fixed bed 2 catalysts which are suitable for the process according to the invention are also compositions of the general formula VI [D]_(p)[E]_(q)  (VI) in which the variables are defined as follows:

-   D=Mo₁₂V_(a″)Z¹ _(b″)Z² _(c″)Z³ _(d″)Z⁴ _(e″)Z⁵ _(f″)Z⁶ _(g″)O_(x″), -   E=Z⁷ ₁₂Cu_(h″)H_(i″)O_(y″), -   Z¹=W, Nb, Ta, Cr and/or Ce, -   Z²=Cu, Ni, Co, Fe, Mn and/or Zn, -   Z³=Sb and/or Bi, -   Z⁴=Li, Na, K, Rb, Cs and/or H, -   Z⁵=Mg, Ca, Sr and/or Ba, -   Z⁶=Si, Al, Ti and/or Zr, -   Z⁷=Mo, W, V, Nb and/or Ta, -   a″=from 1 to 8, -   b″=from 0.2to 5, -   c″=from 0 to 23, -   d″=from 0 to 50, -   e″=from 0 to 2, -   f″=from 0 to 5, -   g″=from 0 to 50, -   h″=from 4 to 30, -   i″=from 0 to 20 and -   x″,y″=numbers which are determined by the valency and frequency of     the elements other than oxygen in VI and -   p,q=numbers other than zero whose p/q ratio is from 160:1 to 1:1,     and which are obtainable by separately preforming a multimetal oxide     composition E     Z⁷ ₁₂Cu_(h″)H_(i″)O_(y″)  (E)     in finely divided form (starting composition 1) and subsequently     incorporating the preformed solid starting composition 1 into an     aqueous solution, an aqueous suspension or into a finely divided dry     mixture of sources of the elements Mo, V, Z¹, Z², Z³, Z⁴, Z⁵, Z⁶     which comprises the abovementioned elements in the stoichiometry D     Mo₁₂V_(a″)Z¹ _(b″)Z² _(c″)Z³ _(d″)Z⁴ _(e″)Z⁵ _(f″)Z⁶ _(g″)  (D)     (starting composition 2) in the desired p:q ratio, drying the     aqueous mixture which may result, and calcining the resulting dry     precursor composition before or after drying at temperatures of from     250 to 600° C. to give the desired catalyst geometry.

Preference is given to the multimetal oxide active compositions VI in which the preformed solid starting composition 1 is incorporated into an aqueous starting composition 2 at a temperature of <70° C. A detailed description of the preparation of multimetal oxide composition III catalysts is contained, for example, in EP-A 668104, DE-A 19736105, and DE-A 19528646.

With regard to the shaping, the statements made for the multimetal oxide IV catalysts apply to the multimetal oxide active composition VI catalysts.

Advantageous multimetal oxide active compositions for the catalysts of the fixed catalyst bed 2 of the process according to the invention are also multielement oxide active compositions of the general formula VII [A]_(p)[B]_(q)[C]_(r)  (VII) in which the variables are each defined as follows:

-   A=Mo₁₂V_(a)X¹ _(b)X² _(c)X³ _(d)X⁴ _(e)X⁵ _(f)X⁶ _(g)O_(x), -   B=X₁ ⁷Cu_(h)H_(i)O_(y), -   C=X₁ ⁸Sb_(j)H_(k)O_(z), -   X¹=W, Nb, Ta, Cr and/or Ce, preferably W, Nb and/or Cr, -   X²=Cu, Ni, Co, Fe, Mn and/or Zn, preferably Cu, Ni, Co and/or Fe, -   X³=Sb and/or Bi, preferably Sb, -   X⁴=Li, Na, K, Rb, Cs and/or H, preferably Na and/or K, -   X⁵=Mg, Ca, Sr and/or Ba, preferably Ca, Sr and/or Ba, -   X⁶=Si, Al, Ti and/or Zr, preferably Si, Al and/or Ti, -   X⁷=Mo, W, V, Nb and/or Ta, preferably Mo and/or W, -   X⁸=Cu, Ni, Zn, Co, Fe, Cd, Mn, Mg, Ca, Sr and/or Ba, preferably Cu     and/or Zn, more preferably Cu, -   a=from 1 to 8, preferably from 2 to 6, -   b=from 0.2 to 5, preferably from 0.5 to 2.5 -   c=from 0 to 23, preferably from 0 to 4, -   d=from 0 to 50, preferably from 0 to 3, -   e=from 0 to 2, preferably from 0 to 0.3, -   f=from 0 to 5, preferably from 0 to 2, -   g=from 0 to 50, preferably from 0 to 20, -   h=from 0.3 to 2.5, preferably from 0.5 to 2, more preferably from     0.75 to 1.5, -   i=from 0 to 2, preferably from 0 to 1, -   j=from 0.1 to 50, preferably from 0.2 to 20, more preferably from     0.2 to 5, -   k=from 0 to 50, preferably from 0 to 20, more preferably from 0 to     12, -   x,y,z=numbers which are determined by the valency and frequency of     the elements in A, B, C other than oxygen, -   p, q=positive numbers -   r=0 or a positive number, preferably a positive number, where the     p/(q+r) ratio=from 20:1 to 1:20, preferably from 5:1 to 1:14 and     more preferably from 2:1 to 1:8 and, in the case that r is a     positive number, the q/r ratio =from 20:1 to 1:20, preferably from     4:1 to 1:4, more preferably from 2:1 to 1:2 and most preferably 1:1,     which contain the fraction [A]_(p) in the form of three-dimensional     regions (phases) A of the chemical composition -   A: Mo₁₂V_(a)X¹ _(b)X² _(c)X³ _(d)X⁴ _(e)X⁵ _(f)X⁶ _(g)O_(x),     the fraction [B]_(q) in the form of three-dimensional regions     (phases) B of the chemical composition -   B: X₁ ⁷Cu_(h)H_(i)O_(y) and     the fraction [C]_(r) in the form of three-dimensional regions     (phases) C of the chemical composition -   C: X₁ ⁸Sb_(j)H_(k)O_(z),     where the regions A, B and, where present, C are distributed     relative to each other as in a mixture of finely divided A, finely     divided B and, where present, finely divided C, and where all     variables are to be selected within the predefined ranges with the     proviso that the molar fraction of the element Mo in the total     amount of all elements in the multielement oxide active composition     VII other than oxygen is from 20 mol % to 80 mol %, the molar ratio     of Mo present in the catalytically active multielement oxide     composition VII, Mo/V, to V present in the catalytically active     multielement oxide composition VII, Mo/V, is from 15:1 to 1:1, the     corresponding molar Mo/Cu ratio is from 30:1 to 1:3 and the     corresponding molar Mo/(total amount of W and Nb) ratio is from 80:1     to 1:4.

Preferred multielement oxide active compositions VII are those whose regions A have a composition within the following stoichiometric pattern of the general formula VIII: Mo₁₂V_(a)X¹ _(b)X² _(c)X⁵ _(f)X⁶ _(g)O_(x)  (VIII) where

-   X¹=W and/or Nb, -   X²=Cu and/or Ni, -   X⁵=Ca and/or Sr, -   X⁶=Si and/or Al, -   a=from 2 to 6, -   b=from 1 to 2, -   c=from 1 to 3, -   f=from 0 to 0.75, -   g=from 0 to 10, and -   x=a number which is determined by the valency and frequency of the     elements in (VIII) other than oxygen.

The term “phase” used in connection with the multielement oxide active compositions VIII means three-dimensional regions whose chemical composition is different to that of their environment. The phases are not necessarily x-ray-homogeneous. In general, phase A forms a continuous phase in which particles of phase B and, where present, C are dispersed.

The finely divided phases B and, where present, C advantageously consist of particles whose largest diameter, i.e. longest line passing through the center of the particles and connecting two points on the surface of the particles, is up to 300 μm, preferably from 0.1 to 200 μm, more preferably from 0.5 to 50 μm and most preferably from 1 to 30 μm. However, particles having a longest diameter of from 10 to 80 μm or from 75 to 125 μm are also suitable.

In principle, the phases A, B and, where present, C may be in amorphous and/or crystalline form in the multielement oxide active compositions VII.

The intimate dry mixtures on which the multielement oxide active compositions of the general formula VII are based and are subsequently to be treated thermally to convert them to active compositions may be obtained, for example, as described in the documents WO 02/24327, DE-A 4405514, DE-A 4440891, DE-A 19528646, DE-A 19740493, EP-A 756894, DE-A 19815280, DE-A 19815278, EP-A 774297, DE-A 19815281, EP-A 668104 and DE-A 19736105.

The basic principle of preparing intimate dry mixtures whose thermal treatment leads to multielement oxide active compositions of the general formula VII is to preform, in finely divided form, separately or combined together, at least one multielement oxide composition B (X₁ ⁷Cu_(h)H_(i)O_(y)) as the starting composition 1 and, where appropriate, one or more multielement oxide compositions C (X₁ ⁸Sb_(j)H_(k)O_(z)) as the starting composition 2, and subsequently to intimately contact, in the desired ratio (corresponding to the general formula VII) the starting compositions 1 and, where appropriate, 2 with a mixture, which comprises sources of the elemental constituents of the multielement oxide composition A Mo₁₂V_(a)X_(b) ¹X_(c) ²X_(d) ³X_(e) ⁴X_(f) ⁵X_(g) ⁶O_(x)  (A) in a composition corresponding to the stoichiometry A, and optionally to dry the resulting intimate mixture.

The intimate contacting of the constituents of the starting compositions 1 and, where appropriate, 2 with the mixture comprising the sources of the elemental constituents of the multimetal oxide composition A (starting composition 3) may be effected either in dry or in wet form. In the latter case, care has to be taken merely that the preformed phases (crystallites) B and, where appropriate, C do not go into solution. In an aqueous medium, the latter is usually ensured at pH values which do not deviate too far from 7 and at temperatures which are not excessively high. When the intimate contacting is effected in wet form, there is normally final drying to give the intimate dry mixture to be thermally treated in accordance with the invention (for example by spray-drying). In the case of dry mixing, such a dry mass is obtained automatically. It will be appreciated that the phases B and, where appropriate, C preformed in finely divided form may also be incorporated into a plastically reshapeable mixture which comprises the sources of the elemental constituents of the multimetal oxide composition A, as recommended by DE-A 10046928. The intimate contacting of the constituents of the starting compositions 1 and, where appropriate, 2 with the sources of the multielement oxide composition A (starting composition 3) may of course also be effected as described in DE-A 19815281.

The thermal treatment to obtain the active composition and the shaping may be effected as described for the multimetal oxide active compositions IV to VI.

Quite generally, multimetal oxide active composition IV to VII catalysts may advantageously be prepared in accordance with the teaching of DE-A 10 325 487 or DE-A 10 325 488.

The performance of the first reaction stage of the process according to the invention, from propene to acrolein, may be carried out with the catalysts described for the fixed catalyst bed 1, in the simplest manner and appropriately from an application point of view, in a tube bundle reactor charged with the fixed bed 1 catalysts, as described, for example, in EP-A 700 714 or DE-A 4 431 949 or WO 03/057653, or WO 03/055835, or WO 03/059857, or WO 03/076373.

In other words, in the simplest manner, the fixed catalyst bed 1 to be used in the process according to the invention is disposed in the uniformly charged metal tubes of a tube bundle reactor and a heating medium (one-zone method), generally a salt melt, is conducted around the metal tubes. Salt melt (heating medium) and reaction gas mixture may be conducted in simple co- or countercurrent. However, the heating medium (the salt melt) may also be conducted around the tube bundle in a meandering manner viewed over the reactor, so that only viewed over the entire reactor does a co- or countercurrent to the flow direction of the reaction gas mixture exist. The volume flow rate of the heating medium (heat exchange medium) is typically such that the temperature rise (caused by the exothermicity of the reaction) of the heat exchange medium from the inlet point into the reactor to the outlet point from the reactor is from 0 to 10° C., frequently from 2 to 8° C., often from 3 to 6° C. The inlet temperature of the heat exchange medium into the tube bundle reactor (in this document, this corresponds to the temperature of the fixed catalyst bed 1) is generally from 250 to 450° C., frequently from 300 to 400° C. or from 300 to 380° C. Suitable heat exchange media are in particular fluid heating media. It is particularly appropriate to use melts of salts such as potassium nitrate, potassium nitrite, sodium nitrite and/or sodium nitrate, or of low-melting metals such as sodium, mercury and also alloys of different metals. Ionic liquids can also be used.

Appropriately, the reaction gas mixture 1 is fed to the charge of fixed bed catalyst preheated to the desired reaction temperature.

Especially in the case of the desired high (e.g. ≧140 l (STP)/l·h or ≧160 l (STP)/l·h, but generally ≦600 l (STP)/l·h) final hourly space velocities of propene on the fixed catalyst bed 1, the process according to the invention is appropriately carried out in a two- or multizone tube bundle reactor (however, it is likewise possible to carry it out in a one-zone tube bundle reactor). A preferred variant of a two-zone tube bundle reactor which can be used for this purpose in accordance with the invention is disclosed by DE-C 2830765. However, the two-zone tube bundle reactors disclosed in DE-C 2513405, U.S. Pat. No. 3147084, DE-A 2201528, EP-A 383224 and DE-A 2903582 are also suitable. Another process description is given by EP-A 1106598.

In other words, in the simplest manner, the fixed catalyst bed 1 to be used in accordance with the invention is disposed in the uniformly charged metal tubes of a tube bundle reactor and two substantially spatially separated heating media, generally salt melts, are conducted around the metal tubes. The tube section over which the particular salt bath extends represents a reaction zone.

For example, a salt bath A preferably flows around that section of the tubes (the reaction zone A) in which the oxidative conversion of propene (in single pass) proceeds until a conversion value in the range from 40 to 80 mol % is achieved and a salt bath B preferably flows around the section of the tubes (reaction zone B) in which the subsequent oxidative conversion of propene (in single pass) proceeds until a conversion value of generally at least 93 mol % is achieved (if required, reaction zones A, B may be followed by further reaction zones which are kept at individual temperatures).

Within the particular temperature zone, the salt bath may in principle be conducted as in the one-zone method. The inlet temperature of the salt bath B is normally from at least 5 to 10° C. above the temperature of the salt bath A. Otherwise, the inlet temperatures may be within the temperature range for the inlet temperature recommended for the one-zone method.

Otherwise, the two-zone high-load method may be carried out as described, for example, in DE-A 10308836, EP-A 1106598, or as described in WO 01/36364, or DE-A 19927624, or DE-A 19948523, DE-A 10313210, DE-A 10313213 or as described in DE-A 19948248.

Accordingly, the process according to the invention is suitable for propene hourly space velocities on the fixed catalyst bed 1 of ≧70 l (STP)/l·h, ≧90 l(STP)/l·h, ≧110 l (STP)/l·h, ≧130 l (STP)/l·h, ≧140 l (STP)/l·h, ≧160 l (STP)/l·h, ≧180 l (STP)/l·h, ≧240 l (STP)/l·h, ≧300 l (STP)/l·h, but normally ≦600 l (STP)/l·h. Here (i.e. generally in the case of propene hourly space velocities in this document), in a departure from the norm in this document, the hourly space velocity is based on the volume of the fixed catalyst bed 1 excluding any sections used which consist exclusively of inert material.

To prepare the fixed catalyst bed 1, it is possible to use in the process according to the invention only the appropriate shaped catalyst bodies having multimetal oxide active composition or else substantially homogeneous mixtures of shaped catalyst bodies having multimetal oxide active composition and shaped bodies having no multimetal oxide active composition which behave substantially inertly with respect to the heterogeneously catalyzed partial gas phase oxidation of propene to acrolein (and consist of inert material) (shaped diluent bodies). Useful materials for such inert shaped bodies are in principle all of those which are also suitable as support materials for first-stage coated catalysts which are suitable in accordance with the invention. Useful such materials are, for example, porous or nonporous aluminum oxides, silicon dioxide, thorium dioxide, zirconium dioxide, silicon carbide, silicates such as magnesium or aluminum silicate or the steatite already mentioned (for example Steatite C-220 from CeramTec).

The geometry of such inert shaped diluent bodies may in principle be as desired. In other words, they may be, for example, spheres, polygons, solid cylinders or else rings.

According to the invention, the inert shaped diluent bodies selected will preferably be those whose geometry-corresponds to that of the first-stage shaped catalyst bodies to be diluted by them.

In general, it is favorable when the chemical composition of the active composition used does not change over the fixed catalyst bed 1. In other words, although the active composition used for an individual shaped catalyst body may be a mixture of different multimetal oxides comprising the elements Mo and/or W and also at least one of the elements Bi, Fe, Sb, Sn and Cu, the same mixture then advantageously has to be used for all shaped catalyst bodies of the fixed catalyst bed 1.

The volume-specific (i.e. normalized to the unit of volume) activity preferably normally increases continuously, abruptly or in stages within the fixed catalyst bed 1 in the flow direction of the starting reaction gas mixture.

The volume-specific activity may, for example, be reduced in a simple manner by homogeneously diluting a basic amount of shaped catalyst bodies prepared in a uniform manner with shaped diluent bodies. The higher the fraction of the shaped diluent bodies selected, the lower the amount of active composition, or catalyst activity, in a certain volume of the fixed bed.

A volume-specific activity increasing at least once in the flow direction of the reaction gas mixture over the fixed catalyst bed 1 can thus be attained in a simple manner for the process according to the invention, for example, by beginning the bed with a high fraction of inert shaped diluent bodies based on one type of shaped catalyst bodies, and then reducing this fraction of shaped diluent bodies in the flow direction either continuously or, once or more than once, abruptly (for example in stages). However, an increase in the volume-specific activity is also possible, for example, by, at constant geometry and active composition type of a shaped coated catalyst body, increasing the thickness of the active composition layer applied to the support, or, in a mixture of coated catalysts having the same geometry but having different proportions by weight of the active composition, increasing the fraction of shaped catalyst bodies having the higher proportion by weight of active composition. Alternatively, the active compositions themselves may also be diluted by, in the course of active composition preparation, for example, incorporating inert diluting materials such as hard-fired silicon dioxide into the dry mixture of starting compounds to be calcined. Different addition amounts of diluting material automatically lead to different activities. The more diluting material is added, the lower the resulting activity will be. A similar effect can also be achieved, for example, by appropriately varying the mixing ratio in mixtures of unsupported catalysts and of coated catalysts (with identical active composition). It will be appreciated that the variants described may also be employed in combination.

Of course, mixtures of catalysts having chemically different active compositions and, as a consequence of this different composition, different activities may also be used for the fixed catalyst bed 1. These mixtures may in turn be diluted with inert diluent bodies.

Upstream and/or downstream of the sections of the fixed catalyst bed 1 having active composition may be disposed beds consisting exclusively of inert material (for example only shaped diluent bodies) (in this document, they are included for terminology purposes in the fixed catalyst bed, unless stated otherwise). These may likewise be brought to the temperature of the fixed catalyst bed 2. The shaped diluent bodies used for the inert bed may have the same geometry as the shaped catalyst bodies used for the sections of the fixed catalyst bed 1 having active composition. However, the geometry of the shaped diluent bodies used for the inert bed may also be different to the aforementioned geometry of the shaped catalyst bodies (for example, spherical instead of annular).

Frequently, the shaped bodies used for such inert beds have the annular geometry 7 mm×7 mm×4 mm (external diameter×length×internal diameter) or the spherical geometry having the diameter d=4–5 mm.

In many cases, the section of the fixed catalyst bed 1 having active composition is structured as follows in the flow direction of the reaction gas mixture in the process according to the invention.

First, to a length of from 10 to 60%, preferably from 10 to 50%, more preferably from 20 to 40% and most preferably from 25 to 35% (i.e., for example, to a length of from 0.70 to 1.50 m, preferably from 0,90 to 1.20 m), each of the total lengths of the section of the fixed bed 1 catalyst charge having active composition, one homogeneous mixture or two successive homogeneous mixtures (having decreasing dilution) of shaped catalyst bodies and shaped diluent bodies (both preferably having substantially the same geometry), in which the proportion by weight of shaped diluent bodies (the mass densities of shaped catalyst bodies and of shaped diluent bodies generally differ only slightly) is normally from 5 to 40% by weight, preferably from 10 to 40% by weight or from 20 to 40% by weight and more preferably from 25 to 35% by weight. Downstream of this first zone is then frequently advantageously disposed, up to the end of the length of the section of the fixed catalyst bed 1 having active composition (i.e., for example, to a length of from 2.00 to 3.00 m, preferably from 2.50 to 3.00 m), either a bed of shaped catalyst bodies diluted only to a lesser extent (than in the first zone), or, most preferably, a sole bed of the same shaped catalyst bodies which have also been used in the first zone.

The aforementioned is especially true when the shaped catalyst bodies used in the fixed catalyst bed 1 are unsupported catalyst rings or coated catalyst rings (especially those which are listed in this document as preferred). For the purposes of the aforementioned structuring, both the shaped catalyst bodies or their support rings and the shaped diluent bodies in the process according to the invention advantageously have substantially the ring geometry 5 mm×3 mm×2 mm (external diameter×length×internal diameter).

The aforementioned is also true when, instead of inert shaped diluent bodies, shaped coated catalyst bodies are used whose active composition content is from 2 to 15% by weight lower than the active composition content of the shaped coated catalyst bodies at the end of the fixed catalyst bed.

A pure inert material bed whose length, based on the total length of the fixed catalyst bed 1, is appropriately from 1 or 5 to 20% generally begins the fixed catalyst bed 1 in the flow direction of the reaction gas mixture. It is normally used as a heating zone for the reaction gas mixture.

Typically, the catalyst tubes in the tube bundle reactors for the first stage are manufactured from ferritic steel and typically have a wall thickness of from 1 to 3 mm. Their internal diameter is generally (uniformly) from 20 to 30 mm, frequently from 21 to 26 mm. Appropriately from an application point of view, the number of catalyst tubes accommodated in the tube bundle reactor is at least 5 000, preferably at least 10 000. Frequently, the number of catalyst tubes accommodated in the reaction vessel is from 15 000 to 30 000. Tube bundle reactors having a number of catalyst tubes above 40 000 are usually exceptional for the first reaction stage. Within the vessel, the catalyst tubes are normally arranged in homogeneous distribution, and the distribution is appropriately selected in such a way that the separation of the central internal axes of immediately adjacent catalyst tubes (known as the catalyst tube pitch) is from 35 to 45 mm (cf., for example, EP-B 468290).

The performance of the second reaction stage of the process according to the invention, from to acrolein to acrylic acid, may be carried out with the catalysts described for the fixed catalyst bed 2, in the simplest manner and appropriately from an application point of view, in a tube bundle reactor charged with the fixed bed 2 catalysts, as described, for example, in EP-A 700 893 or DE-A 4 431 949 or WO 03/057653, or WO 03/055835, or WO 03/059857, or WO 03/076373.

In other words, in the simplest manner, the fixed catalyst bed 2 to be used in the process according to the invention is disposed in the uniformly charged metal tubes of a tube bundle reactor and a heating medium (one-zone method), generally a salt melt, is conducted around the metal tubes. Salt melt (heating medium) and reaction gas mixture may be conducted in simple co- or countercurrent. However, the heating medium (the salt melt) may also be conducted around the tube bundle in a meandering manner viewed over the reactor, so that only viewed over the entire reactor does a co- or countercurrent to the flow direction of the reaction gas mixture exist. The volume flow rate of the heating medium (heat exchange medium) is typically such that the temperature rise (caused by the exothermicity of the reaction) of the heat exchange medium from the inlet point into the reactor to the outlet point from the reactor is from 0 to 10° C., frequently from 2 to 8° C., often from 3 to 6° C. The inlet temperature of the heat exchange medium into the tube bundle reactor (in this document, this corresponds to the temperature of the fixed catalyst bed) is generally from 220 to 350° C., frequently from 245 to 285° C. or from 245 to 265° C. Suitable heat exchange media are in particular fluid heating media. It is particularly appropriate to use melts of salts such as potassium nitrate, potassium nitrite, sodium nitrite and/or sodium nitrate, or of low-melting metals such as sodium, mercury and also alloys of different metals. Ionic liquids can also be used.

Appropriately, the reaction gas mixture 2 is fed to the charge of fixed bed catalyst preheated to the desired reaction temperature.

Especially in the case of the desired high (e.g. ≧140 l (STP)/l·h, but generally ≦600 l (STP)/l·h) final hourly space velocities of acrolein on the fixed catalyst bed 2, the process according to the invention is appropriately carried out in a two- or multizone tube bundle reactor (however, it is likewise possible to carry it out in a one-zone tube bundle reactor). A preferred variant of a two-zone tube bundle reactor which can be used for this purpose in accordance with the invention is disclosed by DE-C 2830765. However, the two-zone tube bundle reactors disclosed in DE-C 2513405, U.S. Pat. No. 3147084, DE-A 2201528, EP-A 383224 and DE-A 2903582 are also suitable.

In other words, in the simplest manner, the fixed catalyst bed 2 to be used in accordance with the invention is disposed in the uniformly charged metal tubes of a tube bundle reactor and two substantially spatially separated heating media, generally salt melts, are conducted around the metal tubes. The tube section over which the particular salt bath extends represents a temperature or reaction zone.

For example, a salt bath C preferably flows around that section of the tubes (the reaction zone C) in which the oxidative conversion of acrolein (in single pass) proceeds until a conversion value in the range from 55 to 85 mol. % is achieved and a salt bath D preferably flows around the section of the tubes (reaction zone D) in which the subsequent oxidative conversion of acrolein (in single pass) proceeds until a conversion value of generally at least 90 mol % is achieved (if required, reaction zones C, D may be followed by further reaction zones which are kept at individual temperatures).

Within the particular temperature zone, the salt bath may in principle be conducted as in the one-zone method. The inlet temperature of the salt bath D is normally from at least 5 to 10° C. above the temperature of the salt bath C. Otherwise, the inlet temperatures may be within the temperature range for the inlet temperature recommended for the one-zone method.

Otherwise, the two-zone high-load method may be carried out as described, for example, in DE-A 19948523, EP-A 1106598 or as described in DE-A 19948248.

Accordingly, the process according to the invention is suitable for acrolein hourly space velocities on the fixed catalyst bed 2 of ≧70 l (STP)/l·h, ≧90 l (STP)/l·h, ≧110 l (STP)/l·h, ≧130 l (STP)/l·h, ≧180 l (STP)/l·h, ≧240 l (STP)/l·h, ≧300 l (STP)/l·h, but normally ≦600 l (STP)/l·h. Here (i.e. generally in the case of acrolein hourly space velocities in this document), in a departure from the norm in this document, the hourly space velocity is based on the volume of the fixed catalyst bed 2 excluding any sections used which consist exclusively of inert material.

To prepare the fixed catalyst bed 2, it is possible to use in the process according to the invention only the appropriate shaped catalyst bodies having multimetal oxide active composition or else substantially homogeneous mixtures of shaped catalyst bodies having multimetal oxide active composition and shaped bodies having no multimetal oxide active composition which behave substantially inertly with respect to the heterogeneously catalyzed partial gas phase oxidation (and consist of inert material) (shaped diluent bodies). Useful materials for such inert shaped bodies are in principle all of those which are also suitable as support materials for second-stage coated catalysts which are suitable in accordance with the invention. Useful such materials are, for example, porous or nonporous aluminum oxides, silicon dioxide, thorium dioxide, zirconium dioxide, silicon carbide, silicates such as magnesium or aluminum silicate or the steatite already mentioned (for example Steatite C-220 from CeramTec).

The geometry of such inert shaped diluent bodies may in principle be as desired. In other words, they may be, for example, spheres, polygons, solid cylinders or else rings. According to the invention, the inert shaped diluent bodies selected will preferably be those whose geometry corresponds to that of the shaped catalyst bodies to be diluted by them.

In general, it is favorable when the chemical composition of the active composition used does not change over the fixed catalyst bed 2. In other words, although the active composition used for an individual shaped catalyst body may be a mixture of different multimetal oxides comprising the elements Mo and V, the same mixture then advantageously has to be used for all shaped catalyst bodies of the fixed catalyst bed 2.

The volume-specific (i.e. normalized to the unit of volume) activity preferably normally increases continuously, abruptly or in stages within the fixed catalyst bed 2 in the flow direction of the reaction gas mixture.

The volume-specific activity may, for example, be reduced in a simple manner by homogeneously diluting a basic amount of shaped catalyst bodies prepared in a uniform manner with shaped diluent bodies. The higher the fraction of the shaped diluent bodies selected, the lower the amount of active composition or catalyst activity, in a certain volume of the fixed bed.

A volume-specific activity increasing at least once in the flow direction of the reaction gas mixture over the fixed catalyst bed 2 can thus be attained in a simple manner for the process according to the invention, for example, by beginning the bed 2 with a high fraction of inert shaped diluent bodies based on one type of shaped catalyst bodies, and then reducing this fraction of shaped diluent bodies in the flow direction either continuously or, once or more than once, abruptly (for example in stages). However, an increase in the volume-specific activity is also possible, for example, by, at constant geometry and active composition type of a shaped coated catalyst body, increasing the thickness of the active composition layer applied to the support, or, in a mixture of coated catalysts having the same geometry but having different proportions by weight of the active composition, increasing the fraction of shaped catalyst bodies having the higher proportion by weight of active composition. Alternatively, the active compositions themselves may also be diluted by, in the course of active composition preparation, for example, incorporating inert diluting materials such as hard-fired silicon dioxide into the dry mixture of starting compounds to be calcined. Different addition amounts of diluting material automatically lead to different activities. The more diluting material is added, the lower the resulting activity will be. A similar effect can also be achieved, for example, by appropriately varying the mixing ratio in mixtures of unsupported catalysts and of coated catalysts (with identical active composition). It will be appreciated that the variants described may also be employed in combination.

Of course, mixtures of catalysts having chemically different active compositions and, as a consequence of this different composition, different activities may also be used for the fixed catalyst bed 2. These mixtures may in turn be diluted with inert diluent bodies.

Upstream and/or downstream of the sections of the fixed catalyst bed 2 having active composition may be disposed beds consisting exclusively of inert material (for example only shaped diluent bodies) (in this document, they are included for terminology purposes in the fixed catalyst bed 2, unless stated otherwise). These may likewise be brought to the temperature of the fixed catalyst bed 2. The shaped diluent bodies used for the inert bed may have the same geometry as the shaped catalyst bodies used for the sections of the fixed catalyst bed 2 having active composition. However, the geometry of the shaped diluent bodies used for the inert bed may also be different to the aforementioned geometry of the shaped catalyst bodies (for example, spherical instead of annular).

Frequently, the shaped bodies used for such inert beds have the annular geometry 7 mm×7 mm×4 mm (external diameter×length×internal diameter) or the spherical geometry having the diameter d=4–5 mm.

In many cases, the section of the fixed catalyst bed 2 having active composition is structured as follows in the flow direction of the reaction gas mixture in the process according to the invention.

First, to a length of from 10 to 60%, preferably from 10 to 50%, more preferably from 20 to 40% and most preferably from 25 to 35% (i.e., for example, to a length of from 0.70 to 1.50 m, preferably from 0,90 to 1.20 m), each of the total lengths of the section of the fixed bed 2 catalyst charge having active composition, one homogeneous mixture or two successive homogeneous mixtures (having decreasing dilution) of shaped catalyst bodies and shaped diluent bodies (both preferably having substantially the same geometry), in which the proportion by weight of shaped diluent bodies (the mass densities of shaped catalyst bodies and of shaped diluent bodies generally differ only slightly) is normally from 10 to 50% by weight, preferably from 20 to 45% by weight and more preferably from 25 to 35% by weight. Downstream of this first zone is then frequently advantageously disposed, up to the end of the length of the section of the fixed catalyst bed 2 having active composition (i.e., for example, to a length of from 2.00 to 3.00 m, preferably from 2.50 to 3.00 m), either a bed of shaped catalyst bodies diluted only to a lesser extent (than in the first zone), or, most preferably, a sole bed of the same shaped catalyst bodies which have also been used in the first zone.

The aforementioned is especially true when the shaped catalyst bodies used in the fixed catalyst bed 2 are coated catalyst rings or coated catalyst spheres (especially those which are listed in this document as preferred). For the purposes of the aforementioned structuring, both the shaped catalyst bodies or their support rings and the shaped diluent bodies in the process according to the invention advantageously have substantially the ring geometry 7 mm×3 mm×4 mm (external diameter×length×internal diameter).

The aforementioned is also true when, instead of inert shaped diluent bodies, shaped coated catalyst bodies are used whose active composition content is from 2 to 15% by weight lower than the active composition content of the shaped coated catalyst bodies at the end of the fixed catalyst bed 2.

A pure inert material bed whose length, based on the total length of the fixed catalyst bed, is appropriately from 5 to 20% generally begins the fixed catalyst bed 2 in the flow direction of the reaction gas mixture. It is normally used as a heating zone for the reaction gas mixture.

Typically, the catalyst tubes in the tube bundle reactors for the second stage are manufactured from ferritic steel and typically have a wall thickness of from 1 to 3 mm. Their internal diameter is generally (uniformly) from 20 to 30 mm, frequently from 21 to 26 mm. Appropriately from an application point of view, the number of catalyst tubes accommodated in the tube bundle reactor is at least 5 000, preferably at least 10 000. Frequently, the number of catalyst tubes accommodated in the reaction vessel is from 15 000 to 30 000. Tube bundle reactors having a number of catalyst tubes above 40 000 are usually exceptional for the first reaction stage. Within the vessel, the catalyst tubes are normally arranged in homogeneous distribution, and the distribution is appropriately selected in such a way that the separation of the central internal axes of immediately adjacent catalyst tubes (known as the catalyst tube pitch) is from 35 to 45 mm (cf., for example, EP-B 468290).

As already described, both reaction stages in the process according to the invention may be carried out in one-zone or in two-zone tube bundle reactors. However, it will be appreciated that only the first reaction stage may be carried out in a one-zone tube bundle reactor and the second reaction stage in a two-zone tube bundle reactor (or vice versa).

Between the tube bundle reactors of the first and the second reaction stage may be disposed an intermediate cooler which may optionally contain inert beds.

It will be appreciated that the fixed catalyst bed 1 and the fixed catalyst bed 2 for the process according to the invention may also be accommodated spatially successively in a single multiple-catalyst-tube tube bundle reactor likewise having, for example, two temperature zones, as described, for example, by WO 03/059857, EP-A 911313 and EP-A 990636. This case is referred to as a single-reactor two-stage process. In this case, one temperature zone generally extends over one fixed catalyst bed. Between the two fixed catalyst beds may additionally be disposed an inert bed which is optionally disposed in a third temperature zone and is heated separately.

The inert gas to be used in the process according to the invention for the charge gas mixture of the first reaction stage (the starting reaction gas mixture 1) may, irrespective of the propene hourly space velocity selected for the fixed catalyst bed 1, consist, for example, of ≧20% by volume, or ≧30% by volume, or ≧40% by volume, or ≧50% by volume, or ≧60% by volume, or ≧70% by volume, or ≧80% by volume, or ≧90% by volume, or ≧95% by volume, of molecular nitrogen.

However, the inert diluent gas may also consist, for example, of from 2 to 35 or 20% by weight of H₂O and from 65 to 98% by volume of N₂.

However, at propene hourly space velocities on the fixed catalyst bed 1 of above 250 l (STP)/l·h, the use is recommended for the process according to the invention of inert diluent gases such as propane, ethane, methane, butane, pentane, CO₂, CO, steam and/or noble gases. However, it will be appreciated that these gases may also be used at lower propene hourly space velocities.

The working pressure in the course of the inventive gas phase partial oxidation of the propene in the first reaction stage may be either below atmospheric pressure (for example up to 0.5 bar) or above atmospheric pressure. Typically, the working pressure in the gas phase partial oxidation of propene will be at values of from 1 to 5 bar, frequently from 1 to 3 bar.

Normally, the reaction pressure in the inventive propene partial oxidation to acrolein will not exceed 100 bar.

The molar O₂:propene ratio in the starting reaction gas mixture 1 which is conducted through the fixed catalyst bed 1 in the process according to the invention will normally be ≧1. Typically, this ratio will be at values of ≦3. According to the invention, the molar O₂:propene ratio in the aforementioned charge gas mixture will frequently be from 1:2 to 1:1.5. In many cases, the process according to the invention will be performed at a propene:oxygen:inert gas (including steam) volume ratio (l(STP)/l·h) in the starting reaction gas mixture 1 of 1:(1 to 3):(3 to 30), preferably of 1:(1.5 to 2.3):(10 to 15).

The propene fraction in the starting reaction gas mixture 1 may lie, for example, at values of from 4 to 20% by volume, frequently from 5 or 7 to 15% by volume or from 6 or 8 to 12% by volume or from 5 to 8% by volume (based in each case on the total volume).

A typical composition of the starting reaction gas mixture 1 (irrespective of the hourly space velocity selected) for the first reaction stage may contain, for example, the following components:

-   -   from 6 to 6.5% by volume of propene,     -   from 3 to 3.5% by volume of H₂O,     -   from 0.3 to 0.5% by volume of CO,     -   from 0.8 to 1.2% by volume of CO₂,     -   from 0.025 to 0.04% by volume of acrolein,     -   from 10.4 to 10.7% by volume of O₂ and     -   as the remainder ad 100%, molecular nitrogen,         or:     -   5.4% by volume of propene,     -   10.5% by volume of oxygen,     -   1.2% by volume of CO_(x),     -   80.5% by volume of N₂ and     -   2.4% by volume of H₂O.

However, the starting reaction gas mixture 1 for the first reaction stage may also have the following composition:

-   -   from 6 to 15% by volume of propene,     -   from 4 to 30% by volume (frequently from 6 to 15% by volume) of         water,     -   from ≧0 to 10% by volume (preferably from ≧0 to 5% by volume) of         constituents other than propene, water, oxygen and nitrogen,     -   sufficient molecular oxygen that the molar ratio of molecular         oxygen present to molecular propene present is from 1.5 to 2.5,         and, as the remainder up to 100% by volume of the total amount,         molecular nitrogen.

Another possible starting reaction gas mixture 1 composition for the first reaction stage may contain:

-   -   6.0% by volume of propene,     -   60% by volume of air and     -   34% by volume of H₂O.

Alternatively, starting reaction gas mixtures 1 of the composition according to Example 1 of EP-A 990 636, or according to Example 2 of EP-A 990 636, or according to Example 3 of EP-A 1 106 598, or according to Example 26 of EP-A 1 106 598, or according to Example 53 of EP-A 1 106 598, may also be used for the first reaction stage.

Further starting reaction gas mixtures 1 for the first reaction stage which are suitable in accordance with the invention may lie within the following composition framework:

-   -   from 7 to 11% by volume of propene,     -   from 6 to 12% by volume of water,     -   from ≧0 to 5% by volume of constituents other than propene,         water, oxygen and nitrogen,     -   sufficient molecular oxygen that the molar ratio of oxygen         present to molecular propene present is from 1.4 to 2.2, and as         the remainder up to 100% by volume of the total amount,         molecular nitrogen.

The propene to be used in the starting reaction gas mixture 1 is in particular polymer-grade propene and chemical-grade propene, as described, for example, by DE-A 10232748.

It should also be mentioned at this point that a portion of the charge gas mixture of the first stage (“propene→acrolein”) may be what is known as cycle gas. This is gas which remains after the product removal in the work-up (acrylic acid removal) which customarily follows the second reaction stage from the product gas mixture of the second reaction stage and is generally recycled partly as a substantially inert diluent gas to charge the first and/or second reaction stage.

The oxygen source used is normally air.

The hourly space velocity on the fixed catalyst bed 1 (here excluding pure inert sections) of starting reaction gas mixture 1 in the process according to the invention will typically be from 1 000 to 10 000 l (STP)/l·h, usually from 1 000 to 5 000l (STP)/l·h, frequently from 1 500 to 4 000 l (STP)/l·h.

After completed intermediate cooling, the product gas mixture of the first reaction stage is optionally fed to the second reaction stage. The oxygen required in the second reaction stage may already have been added to the starting reaction gas mixture 1 for the first reaction stage as an excess and thus be a constituent of the product gas mixture of the first reaction stage. In this case, the optionally intermediately cooled product gas mixture of the first reaction stage may be directly the charge gas mixture of the second reaction stage. However, some or all of the oxygen required for the second oxidation step from acrolein to acrylic acid may also not be added to the product gas mixture of the first reaction stage until it enters the second reaction stage, for example in the form of air. This addition may be associated with the direct cooling of the product gas mixture of the first reaction stage.

Resulting from the aforementioned connection, the inert gas present in the charge gas mixture for the second reaction stage (the starting reaction gas mixture 2) may consist of, for example, ≧20% by volume, or ≧30% by volume, or ≧40% by volume, or ≧50% by volume, or ≧60% by volume, or ≧70% by volume, or ≧80% by volume, or ≧90% by volume, or ≧95% by volume, of molecular nitrogen.

However, the inert diluent gas in the charge gas mixture for the second reaction stage will frequently consist of from 5 to 25 or 20% by weight of H₂O (is formed in the first reaction stage and optionally added) and of from 70 to 90% by volume of N₂.

However, at acrolein hourly space velocities on the fixed catalyst bed 2 of above 250l (STP)/l·h, the use of inert diluent gases such as propane, ethane, methane, butane, pentane, CO₂, steam and/or noble gases is recommended for the process according to the invention. However, it will be appreciated that these gases may also be used even at relatively low acrolein hourly space velocities.

The working pressure in the inventive gas phase partial oxidation of acrolein may be either below atmospheric pressure (for example up to 0.5 bar) or above atmospheric pressure. Typically, the working pressure in the gas phase partial oxidation of acrolein will be at values of from 1 to 5 bar, frequently from 1 to 3 bar.

Normally, the reaction pressure in the inventive acrolein partial oxidation will not exceed 100 bar.

The molar O₂:acrolein ratio in the charge gas mixture for the second reaction stage which is conducted through the fixed catalyst bed 2 in the process according to the invention will normally be ≧1. Typically, this ratio will be at values of ≦3. According to the invention, the molar O₂:acrolein ratio in the aforementioned charge gas mixture will frequently be from 1 to 2 or from 1 to 1.5. In many cases, the process according to the invention will be performed at an acrolein:oxygen:steam:inert gas volume ratio (l(STP)) of 1:(1 to 3):(0 to 20):(3 to 30), preferably of 1:(1 to 3):(0.5 to 10):(7 to 20) in the starting reaction gas mixture 2(charge gas mixture for the second reaction stage).

The acrolein fraction in the charge gas mixture for the second reaction stage may be, for example, at values of from 3 or 6 to 15% by volume, preferably from 4 or 6 to 10% by volume, or from 5 to 8% by volume (based in each case on the total volume). The hourly space velocity on the fixed catalyst bed 2 (excluding pure inert sections) of charge gas mixture (starting reaction gas mixture 2) in the process according to the invention will typically be, as for the first reaction stage, from 1 000 to 10 000 l (STP)/l·h, usually from 1 000 to 5 000 l (STP)/l·h, frequently from 1 500 to 4 000 l (STP)/l·h.

When the process according to the invention is performed, a fresh fixed catalyst bed 1, after it has been conditioned, will normally be operated in such a way that, after determining the composition of the starting reaction gas mixture 1 and determining the hourly space velocity on the fixed catalyst bed 1 of starting reaction gas mixture 1, the temperature of the fixed catalyst bed 1 (or the inlet temperature of the heating medium into the heating zone of the tube bundle reactor) is adjusted in such a way that the conversion C^(pro) of propene on single pass of the reaction gas mixture 1 through the fixed catalyst bed 1 is at least 93 mol %. When favorable catalysts are used, values of C^(pro) of ≧94 mol %, or ≧95 mol %, or ≧96 mol %, or ≧97 mol % and frequently even more are also possible.

When the heterogeneously catalyzed partial oxidation is performed continuously, the composition of the starting reaction gas mixture 1 and the hourly space velocity on the fixed catalyst bed 1 of starting reaction gas mixture 1 will be kept substantially constant (if desired, the hourly space velocity is adapted to the fluctuating market demand). A fall in the activity of the fixed catalyst bed 1 over time will normally be counteracted under these production conditions by increasing the temperature of the fixed catalyst bed (the inlet temperature of the heating medium into the temperature zone of the tube bundle reactor) from time to time (the flow rate of the heating medium is normally likewise kept substantially constant), in order to keep the propene conversion in single pass of the reaction gas mixture within the desired target corridor (i.e. at C^(pro) of ≧93 mol %, or ≧94 mol %, or ≧95 mol %, or ≧96 mol %, or ≧97 mol %). However, such a procedure is accompanied by the disadvantages described at the outset of this document.

The procedure is therefore advantageously to interrupt the gas phase partial oxidation from time to time in accordance with the invention, in order to conduct a gas mixture G consisting of molecular oxygen, inert gas and optionally steam through the fixed catalyst bed 1 at a temperature of the fixed catalyst bed 1 of from 250 to 550° C. Subsequently, the partial oxidation is continued while substantially retaining the process conditions (the propene hourly space velocity on the fixed catalyst bed 1 is preferably restored slowly) and the temperature of the fixed catalyst bed 1 is adjusted in such a way that the propene conversion attains the desired target value. In general, this temperature value, for the same conversion, will be at a somewhat lower value than the temperature that the fixed catalyst bed 1 had before the interruption of the partial oxidation and the inventive treatment with the gas mixture G. Starting from this temperature value of the fixed catalyst bed 1, the partial oxidation is continued while substantially retaining the remaining conditions, and the fall in the activity of the fixed catalyst bed 1 over time will appropriately in turn be counteracted by increasing the temperature of the fixed catalyst bed 1 from time to time. Within, for example, one successive calendar year, the partial oxidation, appropriately in accordance with the invention, is in turn interrupted at least once, in order to conduct the gas mixture G through the fixed catalyst bed 1 in the inventive manner. Afterward, the partial oxidation, advantageously in accordance with the invention, is started up again as described, etc.

In a corresponding manner, when performing the process according to the invention, a fresh fixed catalyst bed 2, after it has been conditioned, will normally be operated in such a way that, after determining the operation of the first reaction stage and the composition of the starting reaction gas mixture 2 and determining the hourly space velocity on the fixed catalyst bed 2 of starting reaction gas mixture 2, the temperature of the fixed catalyst bed 2 (or the inlet temperature of the heating medium into the heating zone of the tube bundle reactor) is adjusted in such a way that the conversion C^(acr) of acrolein in single pass of the starting reaction gas mixture 2 through the fixed catalyst bed 2 is at least 90 mol %. When favorable catalysts are used, values for C^(acr) of ≧92 mol %, or ≧94 mol %, or ≧96 mol %, or ≧98 mol %, and frequently even ≧99 mol % and more are also possible.

When the heterogeneously catalyzed partial oxidation is performed continuously, the composition of the starting reaction gas mixture 2 and the hourly space velocity on the fixed catalyst bed 2 of starting reaction gas mixture 2 will be kept substantially constant (if desired the hourly space velocity is adapted to the fluctuating market demand). A fall in the activity of the fixed catalyst bed 2 over time will normally be counteracted under these production conditions by increasing the temperature of the fixed catalyst bed 2 (the inlet temperature of the heating medium into the temperature zone of the tube bundle reactor) from time to time (the flow rate of the heating medium is likewise normally substantially retained), in order to keep the acrolein conversion in single pass of the charge gas mixture within the desired target corridor (i.e. at values of ≧90 mol %, or ≧92 mol %, or ≧94 mol %, or ≧96 mol %, or ≧98 mol %, or ≧99 mol %). However, such a procedure is associated with the disadvantages described at the outset of this document.

The procedure will therefore, advantageously in accordance with the invention, be to interrupt the gas phase partial oxidation at least once before the predefined temperature increase of the fixed catalyst bed 2 is permanently ≧10° C. or ≧8° C. (based on the temperature of the fixed catalyst bed 2 set beforehand), in order to conduct the gas mixture G through the fixed catalyst bed 2 via the fixed catalyst bed 1 at a temperature of the fixed catalyst bed 2 of from 200 to 450° C. Subsequently, the partial oxidation is continued while substantially retaining the process conditions (the acrolein hourly space velocity on the fixed catalyst bed 2 is preferably restored slowly, as described, for example, in DE-A 10337788) and the temperature of the fixed catalyst bed 2 is adjusted in such a way that the acrolein conversion attains the desired target value. In general, this temperature value, for the same conversion, will be at a somewhat lower value than the temperature that the fixed catalyst bed 2 had before the interruption of the partial oxidation and the inventive treatment with the gas mixture G. Starting from this temperature value of the fixed catalyst bed 2, the partial oxidation is continued while substantially retaining the remaining conditions, and the fall in the activity of the fixed catalyst bed 2 over time is appropriately in turn counteracted by increasing the temperature of the fixed catalyst bed 2 from time to time. Before the temperature increase of the fixed catalyst bed 2 which has been carried out is permanently ≧10° C. or ≧8° C., the partial oxidation is, in accordance with the invention, in turn interrupted at least once, in order to conduct the gas mixture G through the fixed catalyst bed 2 via the fixed catalyst bed 1 in the inventive manner. Afterward, the partial oxidation, advantageously in accordance with the invention, is started up again as described, etc.

It is surprising that in the long-term operation of the inventive two-stage heterogeneously catalyzed gas phase partial oxidation of propene to acrylic acid, the intensity of the hotspot expansions in both reaction stages have more favorable behavior than in prior art processes.

The process according to the invention thus enables on the one hand longer on-stream times of the fixed catalyst beds in the reactor systems before they have to be partly or fully exchanged. On the other hand, the reactant conversions achieved, integrated over time, are likewise increased and the selectivity of target product formations is likewise promoted. To this contributes, for example, the location of the particular hotspot in the process according to the invention either remaining stationary in both reaction stages or, surprisingly, normally migrating in the direction of the inlet point of the charge gas mixture of the particular fixed catalyst bed. The hotspot thus migrates in the particular reaction stage in the reaction gas mixture increasingly into the region in which the acrolein content (1st reaction stage) or acrylic acid content (2nd reaction stage) is still not very pronounced. This reduces the possibility that acrolein which has already formed or acrylic acid which has already formed undergo partial undesired full combustion under the influence of the hotspot temperature. The hotspot temperature can be determined in the process according to the invention in tube bundle reactors, for example, by means of thermal tubes, as described, for example, in EP-A 873 783, WO 03–076373 and in EP-A 1 270 065. The number of such thermal tubes within a tube bundle reactor is appropriately from 4 to 20. Advantageously, they are arranged in uniform distribution within the tube bundle interior.

The process according to the invention is especially advantageous when it is operated at an hourly space velocity on the fixed catalyst bed 1 of propene of ≧110 l (STP)/l·h, or ≧120 l (STP)/l·h, or ≧130 l (STP)/l·h. The acrolein hourly space velocity on the fixed catalyst bed 2 may then in each case be up to 20l (STP)/l·h lower.

Since the gas mixture G in the process according to the invention does not reach the fixed catalyst bed 2 until it has flowed through the fixed catalyst bed 1, it contains in some cases up to 5% by volume of CO at the beginning of the inventive flow-through. It is surprising that this has not been found to be disadvantageous. This CO content normally falls within the period t_(G) from its starting value A to a value E which is less than 50%, preferably less than 35%, more preferably less than 10% or less than 5%, of the starting value A. Most preferably, the CO content C falls within t_(G) to the value E=0.

The aforementioned facts have been found to be advantageous in accordance with the invention.

In the same way, it has been found to be advantageous in the process according to the invention when there is a small content of molybdenum oxide hydrate (in the ppm range) when the gas mixture G enters the fixed catalyst bed 2, said content being discharged in favorable cases by the gas mixture G from the fixed catalyst bed 1 or from molybdenum oxide deposits in the intermediate cooler.

Removal of the acrylic acid from the product gas mixture and accompanying cycle gas formation may be effected as described in WO 97/48669.

Generally, the freshly charged fixed catalyst beds 1 and 2 will be configured in such a way that, as described in EP-A 990636 and EP-A 1106598, both the hotspot development and its temperature sensitivity are very low. Furthermore, both in the case of first startup and in the case of restart after the process according to the invention has been performed, the hourly space velocity on the fixed catalyst beds of reactant will advantageously initially be left at values of ≦100 l (STP)/l·h until steady-state operation has been attained.

EXAMPLES

A) Preparation of the Catalysts Used in the First Reaction Stage

Preparation of an annular unsupported catalyst having the following stoichiometry of reactive metal oxide II: [Bi₂W₂O₉.2WO₃]_(0.5)[Mo₁₂Co_(5.5)Fe_(2.94)Si_(1.59)K_(0.06)O_(x)]₁. 1. Preparation of a Starting Composition 1

209.3 kg of tungstic acid (72.94% by weight of W) were stirred in portions into 775 kg of an aqueous bismuth nitrate solution in nitric acid (11.2% by weight of Bi; free nitric acid from 3 to 5% by weight; mass density: 1.22 to 1.27 g/ml) at 25° C. The resulting aqueous mixture was subsequently stirred at 25° C. for a further 2 h and subsequently spray-dried.

The spray-drying was effected in a rotating disc spray tower in countercurrent at a gas inlet temperature of 300±10° C. and a gas outlet temperature of 100±10° C. The resulting spray powder (particle size a substantially uniform 30 μm) which had an ignition loss of 12% by weight (ignite at 600° C. under air for 3 h) was subsequently converted to a paste in a kneader using 16.8% by weight (based on the powder) of water and extruded by means of an extruder (rotational moment: ≦50 Nm) to extrudates of diameter 6 mm. These were cut into sections of 6 cm, dried under air on a 3-zone belt dryer at a residence time of 120 min at temperatures of 90–95° C. (zone 1), 125° C. (zone 2) and 125° C. (zone 3), and then thermally treated at a temperature in the range from 780 to 810° C. (calcined; in a rotary tube oven flowed through by air (capacity 1.54 m³, 200 m³ (STP) of air/h)). When precisely adjusting the calcination temperature, it is essential that it has to be directed to the desired phase composition of the calcination product. The desired phases are WO₃ (monoclinic) and Bi₂W₂O₉; the presence of γ-Bi₂WO₆ (Russellite) is undesired. Therefore, should the compound γ-Bi₂WO₆ still be detectable by a reflection at a reflection angle of 2θ=28.4° (CuKα radiation) in the x-ray powder diffractogram after the calcination, the preparation has to be repeated and the calcination temperature increased within the temperature range specified or the residence time increased at constant calcination temperature, until the disappearance of the reflection is achieved. The preformed calcined mixed oxide obtained in this way was ground so that the X₅₀ value (cf. Ullmann's Encyclopedia of Industrial Chemistry, 6^(th) Edition (1998) Electronic Release, Chapter 3.1.4 or DIN 66141) of the resulting particle size was 5 mm. The ground material was then mixed with 1% by weight (based on the ground material) of finely divided SiO₂ from Degussa of the Sipernat® type (bulk density 150 g/l; X₅₀ value of the SiO₂ particles was 10 μm, the BET surface area was 100 m²/g).

2. Preparation of a Starting Composition 2

A solution A was prepared by dissolving 213 kg of ammonium heptamolybdate tetrahydrate (81.5% by weight of MoO₃) at 60° C. with stirring in 600 l of water and the resulting solution was admixed while maintaining the 60° C. and stirring with 0.97 kg of an aqueous potassium hydroxide solution (46.8% by weight of KOH) at 20° C.

A solution B was prepared by introducing 116.25 kg of an aqueous iron(III) nitrate solution (14.2% by weight of Fe) at 60° C. into 262.9 kg of an aqueous cobalt(II) nitrate solution (12.4% by weight of Co). Subsequently, while maintaining the 60° C., solution B was continuously pumped into the initially charged solution A over a period of 30 minutes. Subsequently, the mixture was stirred at 60° C. for 15 minutes. 19.16 kg of a Ludox silica gel from Dupont (46.80% by weight of SiO₂, density: from 1.36 to 1.42 g/ml, pH from 8.5 to 9.5, max. alkali content 0.5% by weight) were then added to the resulting aqueous mixture, and the mixture was stirred afterward at 60° C. for a further 15 minutes.

Subsequently, the mixture was spray-dried in countercurrent in a rotating disc spray tower (gas inlet temperature: 400±10° C., gas outlet temperature: 140±5° C.). The resulting spray powder had an ignition loss of approx. 30% by weight (ignite under air at 600° C. for 3 h) and a substantially uniform particle size of 30 μm.

3. Preparation of the Multimetal Oxide Active Composition

The starting composition 1 was mixed homogeneously with the starting composition 2 in the amounts required for a multimetal oxide active composition of the stoichiometry [Bi₂W₂O₉.2WO₃]_(0.5)[Mo₁₂Co_(5.5)Fe_(2.94)Si_(1.59)K_(0.08)O_(x)]₁ in a mixer having bladed heads. Based on the aforementioned overall composition, an additional 1% by weight of finely divided graphite from Timcal AG (San Antonio, US) of the TIMREX P44 type (sieve analysis: min. 50% by weight <24 mm, max. 10% by weight ≧24 μm and ≦48 μm, max. 5% by weight >48 μm, BET surface area: from 6 to 13 m²/g) were mixed in homogeneously. The resulting mixture was then conveyed in a compactor (from Hosokawa Bepex GmbH, D-7421 1 Leingarten) of the K200/100 compactor type having concave, fluted smooth rolls (gap width: 2.8 mm, sieve width: 1.0 mm, lower particle size sieve width: 400 μm, target compressive force: 60 kN, screw rotation rate: from 65 to 70 revolutions per minute). The resulting compactate had a hardness of 10 N and a substantially uniform particle size of from 400 μm to 1 mm.

The compactate was subsequently mixed with, based on its weight, a further 2% by weight of the same graphite and subsequently compressed in a Kilian rotary tableting press of the R×73 type from Kilian, D-50735 Cologne, under a nitrogen atmosphere to give annular shaped unsupported catalyst precursor bodies of the gebmetry (external diameter×length×internal diameter) 5 mm×3 mm×2 mm having a side crushing strength of 19 N±3 N.

In this document, side crushing strength refers to the crushing strength when the annular shaped unsupported catalyst precursor body is compressed at right angles to the cylindrical shell (i.e. parallel to the surface of the ring orifice).

All side crushing strengths in this document relate to a determination by means of a material testing machine from Zwick GmbH & Co. (D-89079 Ulm) of the Z 2.5/TS1S type. This material testing machine is designed for quasistatic stress having a single-impetus, stationary, dynamic or varying profile. It is suitable for tensile, compressive and bending tests. The installed force transducer of the KAF-TC type from A.S.T. (D01307 Dresden) having the manufacturer number 03-2038 was calibrated in accordance with DIN EN ISO 7500–1 and could be used for the 1–500 N measurement range (relative measurement uncertainty: ±0.2%).

The measurements were carried out with the following parameters:

Initial force: 0.5 N.

Rate of initial force: 10 mm/min.

Testing rate: 1.6 mm/min.

The upper die was initially lowered slowly down to just above the cylinder surface of the annular shaped unsupported catalyst precursor body. The upper die was then stopped, in order subsequently to be lowered at the distinctly slower testing rate with the minimum initial force required for further lowering.

The initial force at which the shaped unsupported catalyst precursor body exhibits crack formation is the side crushing strength (SCS).

For the final thermal treatment, in each case 1000 g of the shaped unsupported catalyst precursor bodies were heated in a muffle furnace flowed through by air (capacity 60 l, 1 l/h of air per gram of shaped unsupported catalyst precursor body) from room temperature (25° C.) to 190° C. initially at a heating rate of 180° C./h. This temperature was maintained for 1 h and then increased to 210° C. at a heating rate of 60° C./h. The temperature of 210° C. was in turn maintained over 1 h before it was increased to 230° C. at a heating rate of 60° C./h. This temperature was likewise maintained for 1 h before it was increased to 265° C., again at a heating rate of 60° C./h. The temperature of 265° C. was subsequently likewise maintained over 1 h. Afterward, the furnace was initially cooled to room temperature and the decomposition phase thus substantially completed. The furnace was then heated to 465° C. at a heating rate of 180° C./h and this calcination temperature maintained over 4 h.

Annular unsupported catalysts were obtained from the annular shaped unsupported catalyst precursor bodies.

The specific surface area S, the total pore volume V, the pore diameter d^(max) which makes the greatest contribution to the total pore volume, and the percentages of those pore diameters whose diameter is <0.1 and ≦1 μm in the total pore diameter for the resulting annular unsupported catalysts were as follows:

-   -   S=7.6 [[cm²/g]] m²/g.     -   V=0.27 cm³/g.     -   d^(max)[μm]=0.6.     -   V^(0.1) ¹⁻%=79.

In addition, the ratio R of apparent mass density to true mass density p (as defined in EP-A 1340538) was 0.66.

On the industrial scale, the same annular catalyst was prepared by thermal treatment using a belt calcining apparatus as described in Example 1 of DE-A 10046957 (except that the bed height in the decomposition (chambers 1 to 4) was advantageously 44 mm at a residence time per chamber of 1.46 h and, in the calcination (chambers 5 to 8), it was advantageously 130 mm at a residence time of 4.67 h); the chambers had a surface area (at a uniform chamber length of 1.40 m) of 1.29 m² (decomposition) and 1.40 m² (calcination) and were flowed through from below through the coarse-mesh belt by 75 m³ (STP)/h of supply air which was aspirated by means of rotating ventilators. Within the chambers, the temporal and local deviation of the temperature from the target value was always ≦2° C. Otherwise, the procedure was as described in Example 1 of DE-A 10046957.

B) Preparation of the Catalyst Used in the Second Reaction Stage

1. General Description of the Rotary Tube Furnace Used For Calcination in the Preparation of Starting Compositions 1 and 2

A schematic diagram of the rotary tube furnace is shown by the FIG. 1 appended to this document. The reference numerals which follow relate to this FIG. 1.

The central element of the rotary tube furnace is the rotary tube (1). It is 4 000 mm long and has an internal diameter of 700 mm. It is manufactured from 1.4893 stainless steel and has a wall thickness of 10 mm.

On the interior wall of the rotary tube furnace are mounted lifting lances which have a height of 5 cm and a length of 23.5 cm. They primarily serve the purpose of lifting the material to be thermally treated in the rotary tube furnace, thus mixing it.

At one and the same height of the rotary tube furnace are mounted in each case four lifting lances (a quadruple) equidistantly around the circumference (separation in each case 90°). Along the rotary tube furnace are disposed eight such quadruples (each 23.5 cm apart). The lifting lances of two adjacent quadruples are offset relative to one another on the circumference. At the start and at the end of the rotary tube furnace (first and last 23.5 cm) there are no lifting lances.

The rotary tube rotates freely in a cuboid (2) which has four electrically heated (resistance heating) heating zones which are successive in the length of the rotary tube and are of equal length, each of which encloses the circumference of the rotary tube furnace. Each of the heating zones may heat the appropriate rotary tube section to temperatures between room temperature and 850° C. The maximum heating output of each heating zone is 30 kW. The distance between electrical heating zone and rotary tube exterior surface is about 10 cm. At the start and at the end, the rotary tube projects approx. 30 cm beyond the cuboid.

The rotation rate may be variably adjusted between 0 and 3 revolutions per minute. The rotary tube can be rotated either to the left or to the right. In the case of rotation to the right, the material remains in the rotary tube; in the case of rotation to the left, the material is conveyed from inlet (3) to outlet (4). The inclination angle of the rotary tube to the horizontal may be variably adjusted between 0° and 2°. In batchwise operation, it is in fact 0°. In continuous operation, the lowermost point of the rotary tube is at the material outlet. The rotary tube may be rapidly cooled by switching off the electrical heating zones and switching on a ventilator (5). This aspirates ambient air through holes (6) in the lower base of the cuboid, and conveys it through three flaps (7) having variably adjustable opening in the lid.

The material inlet is controlled via a rotary star feeder (mass control). The material output is, as already mentioned, controlled via the rotation direction of the rotary tube.

In the case of batchwise operation of the rotary tube, an amount of material of from 250 to 500 kg may be thermally treated. The amount is normally disposed exclusively in the heated section of the rotary tube.

From a lance (8) lying on the central axis of the rotary tube, a total of three thermal elements (9) lead vertically into the material at intervals of 800 mm. They enable the determination of the temperature of the material. In this document, temperature of the material refers to the arithmetic mean of the three thermal element temperatures. According to the invention, the maximum deviation of two measured temperatures within the material in the rotary tube is appropriately less than 30° C., preferably less than 20° C., more preferably less than 10° C. and most preferably less than 5 or 3° C.

Gas streams may be conducted through the rotary tube, by means of which the calcination atmosphere or generally the atmosphere of the thermal treatment of the material can be adjusted.

The heater (10) offers the possibility of heating the gas stream conducted into the rotary tube to the desired temperature before its entry into the rotary tube (for example to the temperature desired in the rotary tube for the material). The maximum output of the heater is 1×50 kW+1×30 kW. In principle, the heater (10) may be, for example, an indirect heat exchanger. Such a heater may in principle also be used as a cooler. However, it is generally an electrical heater in which the gas stream is conducted over metal wires heated using electricity (appropriately a 97D/80 CSN flow heater from C. Schniewindt KG, 58805 Neuerade, Germany).

In principle, the rotary tube apparatus provides the possibility of partly or fully recycling the gas stream conducted through the rotary tube. The recycle line required for this purpose is connected to the rotary tube in a mobile manner at the rotary tube inlet and at the rotary tube outlet using ball bearings or using graphite pressure seals. These connections are flushed with inert gas (e.g. nitrogen) (barrier gas). The two flush streams (11) supplement the gas stream conducted through the rotary tube at the inlet into the rotary tube and at the outlet from the rotary tube. Appropriately, the rotary tube narrows at its start and at its end and projects into the tube of the recycle line leading to and away from it respectively.

Downstream of the outlet of the gas stream conducted through the rotary tube is disposed a cyclone (12) to remove solid particles entrained with the gas stream (the centrifugal separator separates solid particles suspended in the gas phase by interaction of centrifugal force and gravity; the centrifugal force of the gas stream rotating as a spiral accelerates the sedimentation of the suspended particles).

The conveying of the cycle gas stream (24) (the gas circulation) is effected by means of a cycle gas compressor (13) (ventilator) which aspirates in the direction of the cyclone and forces in the other direction. Directly downstream of the cycle gas compressor, the gas pressure is generally above one atmosphere. Downstream of the cycle gas compressor is disposed a cycle gas outlet (cycle gas may be discharged via a regulating valve (14)). A diaphragm disposed downstream of the outlet (cross-sectional reduction by about a factor of 3, pressure reducer) (15) eases the discharge.

The pressure downstream of the rotary tube outlet can be controlled via the regulating valve. This is effected in combination with a pressure sensor (16) mounted downstream of the rotary tube outlet, the offgas compressor (17) (ventilator) which aspirates toward the regulating valve, the cycle gas compressor (13) and the fresh gas feed. Relative to the external pressure, the pressure (directly) downstream of the rotary tube outlet may be set, for example, to up to +1.0 mbar higher and, for example, up to −1.2 mbar lower. In other words, the pressure of the gas stream flowing through the rotary tube may be below the ambient pressure of the rotary tube when it leaves the rotary tube.

When the intention is not to at least partly recycle the gas stream conducted through the rotary tube, the connection between cyclone (12) and cycle gas compressor (13) is closed by the three-way valve principle (26) and the gas stream is conducted directly into the offgas cleaning apparatus (23). The connection to the offgas cleaning apparatus disposed downstream of the cycle gas compressor is in this case likewise made by the three-way valve principle. When the gas stream consists substantially of air, it is in this case aspirated (27) via the cycle gas compressor (13). The connection to the cyclone is made by the three-way valve principle. In this case, the gas stream is preferably sucked through the rotary tube, so that the internal rotary tube pressure is less than the ambient pressure.

In the case of continuous operation of the rotary tube furnace apparatus, the pressure downstream of the rotary tube outlet is advantageously set −0.2 mbar below the external pressure. In the case of batchwise operation of the rotary tube apparatus, the pressure downstream of the rotary tube outlet is advantageously set −0.8 mbar below the external pressure. The slightly reduced pressure serves the purpose of preventing contamination of the ambient air with gas mixture from the rotary tube furnace.

Between the cycle gas compressor and the cyclone are disposed sensors (18) which determine, for example, the ammonia content and the oxygen content in the cycle gas. The ammonia sensor preferably operates by an optical measurement principle (the absorption of light of a certain wavelength correlates proportionally to the ammonia content of the gas) and is appropriately an MCS 100 instrument from Perkin & Elmer. The oxygen sensor is based on the paramagnetic properties of oxygen and is appropriately an Oxymat from Siemens of the Oxymat MAT SF 7MB1010-2CA01-1AA1-Z type.

Between the diaphragm (15) and the heater (10), gases such as air, nitrogen, ammonia or other gases may be metered into the cycle gas fraction (19) which is actually to be recirculated. Frequently, a base load of nitrogen is metered in (20). A separate nitrogen/air splitter (21) may be used to react to the measurement of the oxygen sensor.

The discharged cycle gas fraction (22) (offgas) frequently contains gases such as NO_(x), acetic acid, NH₃, etc. which are not completely safe, which is why they are normally removed in an offgas cleaning apparatus (23).

To this end, the offgas is generally initially conducted through a washing column (essentially a column free of internals which contains a separating structured packing upstream of its outlet; the offgas and aqueous sprayed mist are conducted in countercurrent and in cocurrent (2 spray nozzles having opposite spray direction).

Exiting the washing column, the offgas is conducted into an apparatus which contains a fine dust filter (generally a series of bag filters) from whose interior the penetrant offgas is discharged. Finally, incineration is effected in a muffle furnace.

A sensor (28) from KURZ Instruments, Inc., Montery (USA) of the 455 Jr model is used to measure and control the flow rate of the gas stream which is fed to the rotary tube and is different to the barrier gas (measurement principle: thermal-convective mass flow measurement using an isothermal anemometer).

In the case of continuous operation, material and gas phase are conducted through the rotary tube furnace in countercurrent.

In connection with this example, nitrogen always means nitrogen having a purity of >99% by volume.

2. Preparation of the Starting Composition 1 (Phase B) Having the Stoichiometry Cu₁Mo_(0.5)W_(0.5)O₄

98 l of a 25% by weight aqueous NH₃ solution were added to 603 l of water. Subsequently, 100 kg of copper(II) acetate hydrate (content: 40.0% by weight of CuO) were dissolved in the aqueous mixture to give a clear, deep blue aqueous solution 1 which contained 3.9% by weight of Cu and was at room temperature.

Independently of the solution 1, 620 l of water were heated to 40° C. 27.4 kg of ammonium heptamolybdate tetrahydrate (81.5% by weight of MoO₃) were dissolved therein with stirring within 20 min while maintaining the 40° C. 40.4 kg of ammonium paratungstate heptahydrate (88.9% by weight of WO₃) were then added and, after heating to 90° C., dissolved with stirring at this temperature within 45 min. A clear, yellow-orange-colored aqueous solution 2 was obtained.

Subsequently, the aqueous solution 1 was stirred into the solution 2 at 90° C., in the course of which the temperature of the overall mixture did not fall below 80° C. The resulting aqueous suspension was stirred at 80° C. for 30 min. Afterward, it was spray-dried using an S-50-N/R spray dryer from Niro-Atomizer (Copenhagen) (gas inlet temperature: 315° C., gas outlet temperature: 110° C., cocurrent). The spray powder had a particle diameter of from 2 to 50 μm.

100 kg of light green spray powder obtained in this way were metered into a VIU 160 kneader (Sigma blades) from AMK (Aachener Misch- und Knetmaschinen Fabrik) and kneaded with the addition of 8 l of water (residence time: 30 min, temperature: 40 to 50° C.). Afterward, the kneaded material was emptied into an extruder and shaped to extrudates (length: 1–10 cm; diameter: 6 mm) by means of the extruder (from Bonnot Company (Ohio), type: G 103-10/D7A-572K (6″ Extruder W/Packer)). On a belt dryer, the extrudates were dried at a temperature of 120° C. (material temperature) for 1 h. The dried extrudates were subsequently thermally treated (calcined) in the rotary tube furnace described under “1.” as follows:

-   -   the thermal treatment was effected continuously with a material         input of 50 kg/h of extrudates;     -   the inclination angle of the rotary tube to the horizontal was         2°;     -   in countercurrent to the material, an air stream of 75 m³         (STP)/h was conducted through the rotary tube and was         supplemented by a total of (2×25) 50 m³ (STP)/h of barrier gas         at 25° C.;     -   the pressure downstream of the rotary tube outlet was 0.8 mbar         below the external pressure;     -   the rotary tube rotated to the left at 1.5 revolutions/min;     -   no cycle gas method was employed;     -   in the first pass of the extrudates through the rotary tube, the         temperature of the external rotary tube wall was set to 340° C.;         the air stream was conducted into the rotary tube at a         temperature of from 20 to 30° C.;     -   subsequently, the extrudates were conducted through the rotary         tube at the same throughput rate and under the same conditions,         apart from the following differences:         -   the temperature of the rotary tube wall was set to 790° C.;         -   the air stream was conducted into the rotary tube heated to             a temperature of 400° C.

Subsequently, the extrudates having a red-brown color were ground to an average particle diameter of from 3 to 5 μm on a BQ 500 Biplex crossflow classifying mill from Hosokawa-Alpine (Augsburg). The starting composition 1 obtained in this way had a BET surface area of ≦1 m²/g. X-ray diffraction was used to determine the following phases:

-   -   1. CuMoO₄-III having wolframite structure;     -   2. HT copper molybdate.         3. Preparation of the Starting Composition 2 (Phase C) Having         the Stoichiometry CuSb₂O₆

52 kg of antimony trioxide (99.9% by weight of Sb₂O₃) were suspended with stirring in 216 l of water (25° C.). The resulting aqueous suspension was heated to 80° C. Subsequently, stirring was continued while maintaining 80° C. for 20 min. Subsequently, 40 kg of a 30% by weight aqueous hydrogen peroxide solution were added within one hour, in the course of which the temperature of 80° C. was maintained. While maintaining this temperature, stirring was continued for 1.5 hours. 20 l of water at 60° C. were then added to obtain an aqueous suspension 1.618.3 kg of an aqueous ammoniacal copper(II) acetate solution (60.8 g of copper acetate per kg of solution and 75 l of a 25% by weight aqueous ammonium solution in the 618.3 kg of solution) were stirred into this solution at a temperature of 70° C. The mixture was then heated to 95° C. and stirring was continued at this temperature for 30 min. Another 50 1 of water at 70° C. were then added and the mixture was heated to 80° C.

Finally, the aqueous suspension was spray-dried (S-50-N/R spray dryer from Niro-Atomizer (Copenhagen), gas inlet temperature 360° C., gas outlet temperature 110° C., cocurrent). The spray powder had a particle diameter of from 2 to 50 μm.

75 kg of the spray powder obtained in this way were metered into a VIU 160 kneader (Sigma blades) from AMK (Aachener Misch- und Knetmaschinen Fabrik) and kneaded with the addition of 12 l of water (residence time: 30 min, temperature from 40 to 50° C.). Afterward, the kneaded material was emptied into an extruder (same extruder as in phase B preparation) and shaped to extrudates (length 1–10 cm; diameter 6 mm) using the extruder. On a belt dryer, the extrudates were dried at a temperature of 120° C. (material temperature) for 1 h.

250 kg of extrudates obtained in this way were thermally treated (calcined) in the rotary tube furnace described under “1.” as follows:

-   -   the thermal treatment was effected batchwise with a material         amount of 250 kg;     -   the inclination angle of the rotary tube to the horizontal was         ≈0°;     -   the rotary tube rotated to the right at 1.5 revolutions/min;     -   a gas stream of 205 m³ (STP)/h was conducted through the rotary         tube; at the start of the thermal treatment, this consisted of         180 m³ (STP)/h of air and 1×25 m³ (STP)/h of N₂ as barrier gas;         the gas stream leaving the rotary tube was supplemented by a         further 1×25 m³ (STP)/h of N₂; of this overall stream, 22–25% by         volume was recycled into the rotary tube and the remainder         discharged; the discharge amount was replaced by the barrier gas         and the remainder by fresh air;     -   the gas stream was conducted into the rotary tube at 25° C.;     -   the pressure downstream of the rotary tube outlet was 0.5 mbar         below external pressure (atmospheric pressure);     -   the temperature in the material was initially increased linearly         from 25° C. to 250° C. within 1.5 h; the temperature in the         material was then increased linearly from 250° C. to 300° C.         within 2 h and this temperature was maintained for 2 h; then the         temperature in the material was increased linearly from 300° C.         to 405° C. within 3 h and this temperature was subsequently         maintained for 2 h; the heating zones were then switched off and         the temperature within the material was reduced to a temperature         below 100° C. within 1 h and finally to ambient temperature by         activating the rapid cooling of the rotary tube by aspirating         air.

The resulting pulverulent starting composition 2 had a specific BET surface area of 0.6 m²/g and the composition CuSb₂O₆. The powder x-ray digram of the resulting powder showed substantially the refraction angles of CuSb₂O₆ (comparative spectrum 17-0284 of the JCPDS-ICDD-index).

4. Preparation of the Starting Composition 3 Having the Stoichiometry Mo₁₂V_(3.35)W_(1.38)

A stirred tank was initially charged with 900 l of water at 25° C. with stirring. Subsequently, 122.4 kg of ammonium heptamolybdate tetrahydrate (81.5% by weight of MoO₃) were added and the mixture was heated to 90° C. with stirring. Initially 22.7 kg of ammonium metavanadate and finally 22.0 kg of ammonium para-tungstate heptahydrate (88.9% by weight of WO₃) were then stirred in while maintaining the 90° C. Stirring at 90° C. for a total of 80 minutes resulted in a clear orange-colored solution. This was cooled to 80° C. While maintaining the 80° C., initially 18.8 kg of acetic acid (≈100% by weight glacial acetic acid) and then 24 l of 25% by weight aqueous ammonia solution were then stirred in.

The solution remained clear and orange-colored and was spray-dried using an S-50-N/R spray dryer from Niro-Atomizer (Copenhagen) (gas inlet temperature: 260° C., gas outlet temperature: 110° C., cocurrent). The resulting spray powder formed the starting composition 3 and had a particle diameter of from 2 to 50 μm.

5. Preparation of the Dry Composition to be Treated Thermally and Having the Stoichiometry (Mo₁₂V_(3.46)W_(1.39))_(0.87)(CuMo_(0.5)W_(0.5)O₄)_(0.4)(CuSb₂O6)_(0.4)

In a VIU 160 trough kneader having two Sigma blades from AMK (Aachener Mischund Knetmaschinen Fabrik), 75 kg of starting composition 3, 5.2 l of water and 6.9 kg of acetic acid (100% by weight glacial acetic acid) were initially charged and kneaded over 22 min. Subsequently, 3.1 kg of starting composition 1 and 4.7 kg of starting composition 2 were added and kneaded over a further 8 min (T≈40 to 50° C.).

Afterward, the kneaded material was emptied into an extruder (same extruder as in phase B preparation) and shaped to extrudates (length from 1 to 10 cm, diameter 6 mm) using the extruder. These were then dried at a temperature (material temperature) of 120° C. over 1 h on a belt dryer.

306 kg of the dried extrudates were subsequently thermally treated in the rotary tube furnace described under “1.” as follows:

-   -   the thermal treatment was effected batchwise with a material         amount of 306 kg;     -   the inclination angle of the rotary tube to the horizontal was         ≈0°;     -   the rotary tube rotated to the right at 1.5 revolutions/min;     -   initially, the material temperature was heated substantially         linearly from 25° C. to 100° C. within 2 h;     -    during this time, a (substantially) nitrogen stream of 205 m³         (STP)/h is fed through the rotary tube. In the steady state         (after displacement of air which was originally present), this         has the following composition:         -   110 m³ (STP)/h of baseload nitrogen (20),         -   25 m³ (STP)/h of barrier gas nitrogen (11), and         -   70 m³(STP)/h of recirculated cycle gas (19).

The barrier gas nitrogen was fed at a temperature of 25° C. The mixture of the two other nitrogen streams was conducted into the rotary tube in each case at the temperature that the material·had in each case in the rotary tube.

-   -   subsequently, the material temperature was increased from         100° C. to 320° C. at a heating rate of 0.7° C./min;     -    until a material temperature of 300° C. had been attained, a         gas stream of 205 m³ (STP)/h was conducted through the rotary         tube and had the following composition:         -   110 m³ (STP)/h consisting of baseload nitrogen (20) and             gases released in the rotary tube,         -   25 m³ (STP)/h of barrier gas nitrogen (11) and         -   70 m³(STP)/h of recirculated cycle gas (19).

The barrier gas nitrogen was fed at a temperature of 25° C. The mixture of the two other gas streams was conducted into the rotary tube in each case at the temperature that the material had in each case in the rotary tube.

From the exceeding of the material temperature of 160° C. to the attainment of a material temperature of 300° C., 40 mol % of the total amount of ammonia M^(A) released in the course of the overall thermal treatment of the material was released from the material.

-   -   on attainment of the material temperature of 320° C., the oxygen         content of the gas stream fed to the rotary tube was increased         from 0% by volume to 1.5% by volume and maintained over the         following 4 h.

At the same time, the temperature in the four heating zones heating the rotary tube was reduced by 5° C. (to 325° C.) and maintained thus over the following 4 h.

The material temperature passed through a temperature maximum above 325° C. which did not exceed 340° C. before the material temperature fell back to 325° C.

The composition of the gas stream conducted through the rotary tube of 205 m³ (STP)/h was changed as follows over this period of 4 h:

-   -   95 m³ (STP)/h consisting of baseload nitrogen (20) and gases         released in the rotary tube;     -   25 m³ (STP)/h of barrier gas nitrogen (11);     -   70 m³ (STP)/h of recirculated cycle gas; and     -   15 m³ (STP)/h of air via the splitter (21).

The barrier gas nitrogen was fed at a temperature of 25° C. The mixture of the other gas streams was in each case conducted into the rotary tube at the temperature that the material·had in each case in the rotary tube.

From the exceeding of the material temperature of 300° C. until the 4 h had elapsed, 55 mol % of the total amount of ammonia released M^(A) in the course of the overall thermal treatment of the material was released from the material (a total of 40 mol %+55 mol %=95 mol % of the amount of ammonia M^(A) had thus been released before 4 h had elapsed).

-   -   when the 4 h had elapsed, the temperature of the material was         increased to 400° C. within about 1.5 h at a heating rate of         0.85° C./min.

Subsequently, this temperature was maintained for 30 min.

The composition of the gas stream fed to the rotary tube of 205 m³ (STP)/h over this time was as follows:

-   -   95 m³ (STP)/h composed of baseload nitrogen (20) and gases         released in the rotary tube;     -   15 m³(STP)/h of air (splitter (21));     -   25 m³ (STP)/h of barrier gas nitrogen (11); and     -   70 m³ (STP)/h of recirculated cycle gas.

The barrier gas nitrogen was fed at a temperature of 25° C. The mixture of the other gas streams was in each case conducted into the rotary tube at the temperature that the material·had in each case in the rotary tube.

-   -   reducing the temperature of the material ended the calcination;         to this end, the heating zones were switched off and the rapid         cooling of the rotary tube by aspirating air was switched on,         and the material temperature was reduced to a temperature below         100° C. within 2 h and finally to ambient temperature; with the         switching-off of the heating zones, the composition of the gas         stream fed to the rotary tube of 205 m³ (STP)/h was changed to         the following mixture:     -   110 m³ (STP)/h composed of baseload nitrogen (20) and gases         released in the rotary tube;     -   0 m³ (STP)/h of air (splitter (21));     -   25 m³(STP)/h of barrier gas nitrogen (11); and     -   70 m³ (STP)/h of recirculated cycle gas.

The gas stream was fed to the rotary tube at a temperature of 25° C.

-   -   over the entire thermal treatment, the pressure (immediately)         downstream of the rotary tube outlet was 0.2 mbar below the         external pressure.         6. Shaping of the Multimetal Oxide Active Composition

The catalytically active material obtained in “5.” was ground using a BQ 500 Biplex cross flow classifying mill (Hosokawa-Alpine Augsburg) to a finely divided powder of which 50% of the powder particles passed through a sieve of mesh width from 1 to 10 μm and whose fraction of particles having a largest dimension above 50 μm was less than 1%.

The ground powder was used as in S1 of EP-B 714700 to coat annular support bodies (external diameter 7 mm, length 3 mm, internal diameter 4 mm, steatite of the type C220 from CeramTec having a surface roughness Rz of 45 μm). The binder was an aqueous solution of 75% by weight of water and 25% by weight of glycerol.

However, the selected active composition fraction of the resulting coated catalysts was, in contrast to the aforementioned example S1, 20% by weight (based on the total weight of support body and active composition). The ratio of powder and binder was adapted proportionately.

FIG. 2 shows the percentage of M^(A) as a function of the material temperature in ° C. FIG. 3 shows the ammonia concentration of the atmosphere A in % by volume over the thermal treatment as a function of the material temperature in ° C.

C) Performance of the Partial Oxidation

I. Description of the General Process Conditions in the First Reaction Stage

Heat exchange medium used: Salt melt consisting of 60% by weight of potassium nitrate and 40% by weight of sodium nitrite.

Material of the catalyst tubes: ferritic steel.

Dimensions of the catalyst tubes: Length 3200 mm; internal diameter 25 mm; external diameter 30 mm (wall thickness: 2.5 mm).

Number of catalyst tubes in the tube bundle: 25 500.

Reactor: Cylindrical vessel of diameter 6800 mm; annularly arranged tube bundle having a free central space.

-   -   Diameter of the central free space: 1000 mm. Distance of the         outermost catalyst tubes from the vessel wall: 150 mm.         Homogeneous catalyst tube distribution in the tube bundle (6         equidistant neighboring tubes per catalyst tube).     -   Catalyst tube pitch: 38 mm.     -   The catalyst tubes were secured and sealed by their ends in         catalyst tube plates of thickness 125 mm and opened with their         orifices each into a hood connected to the vessel at the upper         or lower end.     -   Feed of the heat exchange medium to the tube bundle:     -   The tube bundle was divided by three deflecting plates         (thickness in each case 10 mm) mounted in succession between the         catalyst tube plates in the longitudinal direction into 4         equidistant (each 730 mm) longitudinal sections (zones).

The uppermost and the lowermost deflecting plate had annular geometry, the internal annular diameter was 1000 mm and the external annular diameter extended with sealing to the vessel wall. The catalyst tubes were not secured and sealed to the deflecting plates. Rather, a gap having a gap width of <0.5 mm was left in such a way that the transverse flow rate of the salt melt was substantially constant within one zone.

The middle deflecting plate was circular and extended up to the outermost catalyst tubes of the tube bundle.

The recycling of the salt melt was brought about by two salt pumps, each of which supplied one longitudinal half of the tube bundle.

The pumps compressed the salt melt into an annular channel which was arranged at the bottom around the reactor jacket and divided the salt melt over the vessel circumference. The salt melt reached the tube bundle in the lowermost longitudinal section through windows in the reactor jacket. The salt melt then flowed as dictated by the deflecting plates in the sequence

-   -   from the outside inward,     -   from the inside outward,     -   from the outside inward,     -   from the inside outward,         in a substantially meandering manner, viewed over the vessel,         from bottom to top. The salt melt collected through windows         mounted in the uppermost longitudinal section around the vessel         circumference in an annular channel mounted at the top around         the reactor jacket and, after cooling to the original inlet         temperature, was compressed back into the lower annular channel         by the pumps.

The composition of the starting reaction gas mixture 1 (mixture of air, chemical-grade propylene and cycle gas) over the operating time was within the following framework:

-   -   from 5 to 7% by volume of chemical-grade propene,     -   from 10 to 14% by volume of oxygen,     -   from 1 to 2% by volume of CO_(x),     -   from 1 to 3% by volume of H₂O, and     -   at least 80% by volume of N₂.

Reactor charge: Salt melt and reaction gas mixture were conducted in countercurrent viewed over the reactor. The salt melt entered at the bottom, the reaction gas mixture at the top.

-   -   The inlet temperature of the salt melt was 337° C. at the start         (on completion of conditioning of the fixed catalyst bed).     -   The outlet temperature of the salt melt was 339° C. at the         start.     -   The pump output was 6 200 m³ of salt melt/h.     -   The starting reaction gas mixture was fed to the reactor at a         temperature of 300° C.

Propene loading of the fixed catalyst bed 1: from 90 to 120 l (STP)/l·h

Catalyst tube charge with fixed catalyst bed 1 (from top to bottom): Zone A: 50 cm

-   -   Preliminary bed of steatite rings of geometry 7 mm×7 mm×4 mm         (external diameter×length×internal diameter)     -   Zone B: 100 cm catalyst charge with a homogeneous mixture of 30%         by weight of steatite rings of geometry 5 mm×3 mm×2 mm (external         diameter×length×internal diameter) and 70% by weight of the         annular unsupported catalyst prepared for the first reaction         stage).

Zone C: 170 cm catalyst charge with the annular (5 mm×3 mm×2 mm=external diameter×length×internal diameter) unsupported catalyst prepared for the first reaction stage.

The thermal tubes (their number was 10 which were uniformly distributed in the central region of the tube bundle) were configured and charged as follows: (they were used to determine the hotspot temperature; this is an arithmetic average of independent measurements in the 10 thermal tubes)

Each of the 10 thermal tubes had a central thermowell having 40 temperature measurement points (i.e. each thermal tube contained 40 thermo elements which were integrated into a thermowell at different lengths and thus formed a multithermo element by which the temperature could be simultaneously determined within the thermal tube at different heights).

At least 13 and at most 30 of the in each case 40 temperature measurement points were in the region of the first meter of the active section of the fixed catalyst bed (in the flow direction of the reaction gas mixture).

The internal diameter of a thermal tube was 27 mm. The wall thickness and tube material were as in the working tubes.

The external diameter of the thermowell was 4 mm.

The thermal tubes were charged as follows:

A thermal tube was charged with the annular unsupported catalyst prepared. In addition, catalyst spall which had been generated from the annular unsupported catalyst and had a longest dimension of from 0.5 to 5 mm was charged into the thermal tube.

The catalyst spall was charged in homogeneous distribution over the entire active section of the fixed catalyst bed of the particular thermal tube in such a way that the pressure drop of the reaction gas mixture as it passed through the thermal tube corresponded to that as the reaction gas mixture passed through a working tube (for this purpose, from 5 to 20% by weight of catalyst spall were required based on the active section of the fixed catalyst bed (i.e. excluding the inert sections) in the thermal tube). At the same time, the particular total fill height of active and inert sections in the working and thermal tubes was the same and the ratio of the total amount of active composition present in the tube to heat exchange surface area of the tube in working and thermal tubes was set at substantially the same value.

II. Description of the Intermediate Cooling

The product gas mixture leaving the first reaction stage at a temperature corresponding to the salt melt outlet temperature was, for the purpose of intermediate cooling, conducted through a one-zone tube bundle heat exchanger made of ferritic steel which was cooled with a salt melt composed of 60% by weight of potassium nitrate and 40% by weight of sodium nitrite and had been flanged directly onto the reactor. The separation of the lower tube plate of the reactor from the upper tube plate of the cooler was 10 cm. The salt melt and the product gas mixture, viewed over the heat exchanger, were conducted in countercurrent. The salt bath itself flowed, in the same manner as in the first-stage one-zone multiple catalyst tube fixed bed reactor, in a meandering manner around the cooling tubes through which the product gas mixture was passed. The length of the cooling tubes was 1.65 m, their internal diameter was 2.6 cm and their wall thickness was 2.5 mm. The number of cooling tubes was 8 000. The diameter of the heat exchanger was 7.2 m.

They were distributed uniformly over the cross section with uniform tube pitch.

Into the inlet of the cooling tubes (in flow direction) were introduced spirals of stainless steel whose cross section corresponded virtually to that of the cooling tubes. Their length was from 700 mm to 1000 mm (alternatively, the cooling tubes may be filled with large inert material rings). They served to improve the heat transfer.

The product gas mixture left the intermediate cooler at a temperature of 250° C. Subsequently, compressed air which had a temperature of 140° C. was mixed with it in an amount of about 6700 m³ (STP)/l·h, so that the composition described hereinbelow of the charge gas mixture for the second reaction stage resulted.

The resulting charge gas mixture (starting reaction gas mixture 2) was fed to the one-zone multiple catalyst tube fixed bed reactor of the second reaction stage at a temperature of 220° C.

III. Description of the General Process Conditions in the Second Reaction Stage

A one-zone multiple catalyst tube fixed bed reactor was used which had the same design as that of the first stage.

The composition of the charge gas mixture (starting reaction gas mixture 2) was within the following framework over the operating time:

from 4 to 6% by volume of acrolein,

from 5 to 8% by volume of O₂,

from 1.2 to 2.5% by volume of CO_(x),

from 6 to 10% by volume of H₂O and

at least 75% by volume of N₂.

Reactor charge: Salt melt and charge gas mixture were conducted in countercurrent viewed over the reactor. The salt melt entered from the bottom, the charge gas mixture from the top.

-   -   The inlet temperature of the salt melt at the start (on         completion of conditioning of the fixed catalyst bed 2) was         approx. 263° C. The accompanying outlet temperature of the salt         melt was approx. 265° C. at the start.     -   The pump output was 6200 m³ of salt melt/h.     -   The starting reaction gas mixture was fed to the reactor at a         temperature of 240° C.

Acrolein loading of the fixed catalyst bed 2: from 95 to 110 l (STP)/l·h

The catalyst tube charge with fixed catalyst bed 2 (from top to bottom) was: Zone A: 20 cm preliminary bed of steatite rings of geometry 7 mm×7 mm×4 mm (external diameter×length×internal diameter).

-   -   Zone B:

100 cm catalyst charge of a homogeneous mixture of 25% by weight of steatite rings of geometry 7 mm×3 mm×4 mm (external diameter×length×internal diameter) and 75% by weight of the annular (approx. 7 mm×3 mm×4 mm) coated catalyst prepared for the second reaction stage.

-   -   Zone C: 200 cm catalyst charge of the annular (approx. 7 mm×3         mm×4 mm) coated catalyst prepared for the second reaction stage.

The thermal tubes (their number was 10 which were uniformly distributed in the central region of the tube bundle) were configured and charged as follows: (they were used to determine the hotspot temperature; this is an arithmetic average of independent measurements in the 10 thermal tubes)

Each of the 10 thermal tubes had a central thermowell having 40 temperature measurement points (i.e. each thermal tube contained 40 thermo elements which were integrated into a thermowell at different lengths and thus formed a multithermo element by which the temperature could be simultaneously determined within the thermal tube at different heights).

At least 13 and at most 30 of the in each case 40 temperature measurement points were in the region of the first meter of the active section of the fixed catalyst bed (in the flow direction of the reaction gas mixture).

The internal diameter of a thermal tube was 27 mm. The wall thickness and tube material were as in the working tubes.

The external diameter of the thermowell was 4 mm.

The thermal tubes were charged as follows:

A thermal tube was charged with the annular coated catalyst prepared. In addition, spherical coated catalyst (same active composition as the annular coated catalyst, the diameter of the Steatite C220 (CeramTec) support spheres was 2–3 mm; the active composition fraction was 20% by weight, the preparation was as described for the annular unsupported catalyst, except that the binder was an appropriate amount of water) was charged into the thermal tube.

The spherical coated catalyst was charged in homogeneous distribution over the entire active section of the fixed catalyst bed of the particular thermal tube, in such a way that the pressure drop of the reaction gas mixture as it passed through the thermal tube corresponded to that when the reaction gas mixture passed through a working tube (based on the active section of the fixed catalyst bed (i.e. excluding the inert sections); for this purpose, from 5 to 20% by weight of spherical coated catalyst were required in the thermal tube). At the same time, the particular total fill height of active and inert sections in the working and thermal tubes was the same and the ratio of the total amount of active composition present in the tube to heat exchange surface area of the tube in working or thermal tubes was set at the same value.

III. Long-term Operation (Results)

The target conversion for the propene to be converted in single pass of the reaction gas mixture 1 through the fixed catalyst bed 1 was set at 97.5 mol %.

Successive increases in the inlet temperature of the salt melt into the first-stage reactor allowed this conversion value to be maintained over time when the process was carried out continuously.

The target conversion for the acrolein to be converted in single pass of the starting reaction gas mixture 2 through the fixed catalyst bed 2 was set at 99.3 mol %.

Successive increases in the inlet temperature of the salt melt into the second-stage reactor allowed this conversion value to be maintained over time when the process was carried out continuously.

Once per calendar month the partial oxidation was interrupted (the increase in the inlet temperature of the salt melt in the second-stage reactor up to the monthly interruption was always ≧0.3° C. and ≦4° C.; in the case of the first-stage reactor, the increase values required per month were ≧0.5° C.), the inlet temperature of the salt melt which was last employed in the particular reaction stage and in the intermediate cooler was maintained and a gas mixture G composed of 6% by volume of O₂ and 95% by volume of N₂ was conducted through the entire reactor system at an hourly space velocity on the fixed catalyst bed 1 of 30 l (STP)/l·h for a period t_(G) of from 24 h to 48 h.

Afterward, the partial oxidation was continued and the inlet temperatures of the salt melt into the particular reaction stage were adjusted in such a way that the target conversion of the particular reaction stage was still attained.

The inlet temperatures of the salt melts and the hotspot temperatures and also the selectivity S^(AC+AA) of the sum of acrolein formation and acrylic acid by-production in the first reaction stage and the selectivity S^(AA) of acrylic acid formation in the second reaction stage (based in each case on converted propene) developed as follows:

First reaction stage: Start: Salt melt inlet temperature = 316° C. Hotspot temperature = 366° C. S^(AC+AA) = 94.5 mol % after 1 year of Salt melt inlet temperature = 319° C. operating time: Hotspot temperature = 370° C. S^(AC+AA) = 94.8 mol % after 2 years of Salt melt inlet temperature = 324° C. operating time: Hotspot temperature = 371° C. S^(AC+AA) = 95.1 mol % after 3 years of Salt melt inlet temperature = 330° C. operating time: Hotspot temperature = 376° C. S^(AC+AA) = 95.4 mol % Second reaction stage: Start: Salt melt inlet temperature = 263° C. Hotspot temperature = 290° C. S^(AA) = 89.2 mol % After 1 year of Salt melt inlet temperature = 268° C. operating time: Hotspot temperature = 292° C. S^(AA) = 89.4 mol % After 2 years of Salt melt inlet temperature = 274° C. operating time: Hotspot temperature = 297° C. S^(AA) = 89.7 mol % After 3 years of Salt melt inlet temperature = 278° C. operating time: Hotspot temperature = 300° C. S^(AA) = 90.2 mol %

The temperature data (apart from the start) relate in all cases to the time in each case which was just before the interruption of the partial oxidation and the treatment of the catalyst beds with the gas mixture G.

Within the 3 years of operating time, the location of the hotspot temperature in the fixed catalyst bed 2 migrated by approx. 25 cm in the direction of the inlet point of the charge gas mixture.

The example may also be carried out in a corresponding manner with a starting reaction gas mixture 1 for the first reaction stage having the following composition:

-   -   6.0% by volume of propene,     -   60% of volume of air and     -   34% of volume of H₂O.

Alternatively, starting reaction gas mixtures 1 used for the first reaction stage may also be of the composition according to Example 1 of EP-A 990 636 or according to Example 2 of EP-A 960 636 or according to Example 3 of EP-A 1 106 598 or according to Example 26 of EP-A 1 106 598 or according to Example 53 of EP-A 1 106 598. There is only secondary air feeding to the extent that O₂.C₃H₄O≧0.5 and ≦1.5 is fulfilled in the charge gas for the second reaction stage (starting reaction gas mixture 2).

U.S. Provisional Patent Application No. 60/515,659, filed on Oct. 31, 2003, is incorporated into the present application by literature reference.

With reference to the abovementioned teachings, numerous alterations and deviations from the present invention are possible. It may therefore be assumed that the invention within the scope of the appended claims, may be performed differently to the way specifically described herein. 

1. A process for the long-term operation of a heterogeneously catalyzed gas phase partial oxidation of propene to acrylic acid, by initially conducting a starting reaction gas mixture 1 which comprises propene, molecular oxygen and at least one inert gas and contains the molecular oxygen and the propene in a molar O₂:C₃H₆ ratio of ≧1, in a first reaction stage, at elevated temperature, over a first fixed catalyst bed 1 whose catalysts are such that their active composition is at least one multimetal oxide containing molybdenum and/or tungsten and also at least one of the elements bismuth, tellurium, antimony, tin and copper, in such a way that the propene conversion in single pass is 93 mol % and the accompanying selectivity of acrolein formation and of acrylic acid by-production taken together are 90 mol %, optionally reducing the temperature of the product gas mixture 1 leaving the first reaction stage by direct and/or indirect cooling and optionally adding molecular oxygen and/or inert gas to the product gas mixture 1, and then conducting the product gas mixture 1, as a starting reaction gas mixture 2 which comprises acrolein, molecular oxygen and at least one inert gas and contains the molecular oxygen and the acrolein in a molar O₂:C₃H₄O ratio of ≧0.5, in a second reaction stage, at elevated temperature, over a second fixed catalyst bed 2 whose catalysts are such that their active composition is at least one multimetal oxide containing the elements molybdenum and vanadium, in such a way that the acrolein conversion in single pass is ≧90 mol % and the selectivity of acrylic acid formation assessed over both reaction stages, based on propene converted, is ≧80 mol %, and by, in order to counteract the deactivation both of the fixed catalyst bed 1 and of the fixed catalyst bed 2, independently increasing the temperature of the particular fixed catalyst bed over time, which comprises interrupting the gas phase partial oxidation at least once before the temperature increase of the fixed catalyst bed 2 is permanently ≧10° C., and, at a temperature of the fixed catalyst bed 1 of from 250 to 550° C. and a temperature of the fixed catalyst bed 2 of from 200 to 450° C. initially conducting a gas mixture G consisting of molecular oxygen, inert gas and optionally steam through the fixed catalyst bed 1, and subsequently optionally through an intermediate cooler and finally through the fixed catalyst bed 2, wherein said temperature increase is first based on the temperature of the fixed catalyst bed 2 set at the beginning of the process and subsequently based on said temperature after each said interruption and conducting of gas mixture G through said catalyst beds.
 2. A process as claimed in claim 1, wherein the gas phase partial oxidation is interrupted at least once before the temperature increase of the fixed catalyst bed 2 is permanently 8° C. and the gas mixture G is conducted through the catalyst beds.
 3. A process as claimed in claim 1, wherein the period over which the gas mixture G is conducted through the fixed catalyst beds is from 2 h to 120 h.
 4. A process as claimed in claim 1, wherein the gas mixture G which is conducted through the fixed catalyst beds contains at least 4% by volume of oxygen.
 5. A process as claimed in claim 1, wherein the active composition of the catalysts of the fixed catalyst bed 1 is at least one multimetal oxide of the general formula I Mo₁₂Bi_(a)Fe_(b)X¹ _(c)X² _(d)X³ _(e)X⁴ _(f)O_(n)  (I) in which the variables are each defined as follows: X¹=nickel and/or cobalt, X²=thallium, an alkali metal and/or an alkaline earth metal, X³=zinc, phosphorus, arsenic, boron, antimony, tin, cerium, lead and/or tungsten, X⁴=silicon, aluminum, titanium and/or zirconium, a=from 0.5 to 5, b=from 0.01 to 5, c=from 0 to 10, d=from 0 to 2, e=from 0 to 8, f=from 0 to 10 and n=a number which is determined by the valency and frequency of the elements in I other than oxygen.
 6. A process as claimed in any of claim 1, wherein the active composition of the catalysts of the fixed catalyst bed 2 is at least one multimetal oxide of the general formula IV Mo₁₂V_(a)X¹ _(b)X² _(c)X³ _(d)X⁴ _(e)X⁵ _(f)X⁶ _(g)O_(n)  (IV) in which the variables are each defined as follows: X¹=W, Nb, Ta, Cr and/or Ce, X²=Cu, Ni, Co, Fe, Mn and/or Zn, X³=Sb and/or Bi, X⁴=one or more alkali metals, X⁵=one or more alkaline earth metals, X⁶=Si, Al, Ti and/or Zr, a=from 1 to 6, b=from 0.2 to 4, c=from 0.5 to 18, d=from 0 to 40, e=from 0 to 2, f=from 0 to 4, g=from0 to 40 and n=a number which is determined by the valency and frequency of the elements in IV other than oxygen.
 7. A process as claimed in claim 1, wherein the propene hourly space velocity on the fixed catalyst bed 1 is ≧90 l (STP)/l.h.
 8. A process as claimed in claim 1, wherein the propene hourly space velocity on the fixed catalyst bed 1 is ≧130 l (STP)/l.h.
 9. A process as claimed in claim 1, wherein the propene content in the starting reaction gas mixture 1 is from 7 to 15% by volume.
 10. A process as claimed in 1, wherein the propene content in the starting reaction gas mixture 1 is from 8 to 12% by volume.
 11. A process as claimed in claim 1, wherein the acrolein content in the starting reaction gas mixture 2 is from 6 to 15% by volume.
 12. A process as claimed in claim 1, wherein the increase in the temperature of the fixed catalyst bed 1 over time is carried out in such a way that the propene content in the product gas mixture 1 of the first reaction stage does not exceed 10 000 ppm by weight.
 13. A process as claimed in claim 1, wherein the increase in the temperature of the fixed catalyst bed 1 over the time is carried out in such a way that the conversion of propene in single pass of the reaction gas mixture 1 through the fixed catalyst bed 1 does not go below 94 mol %.
 14. A process as claimed in claim 1, wherein the increase in the temperature of the fixed catalyst bed 2 over the time is carried out in such a way that the acrolein content in the product gas mixture of the second reaction stage does not exceed 1 500 ppm by weight.
 15. A process as claimed in claim 1, wherein the increase in the temperature of the fixed catalyst bed 2 over the time is carried out in such a way that the conversion of acrolein in single pass of the reaction gas mixture through the fixed catalyst bed 2 does not go below 92 mol %.
 16. A process as claimed in claim 1, wherein both reaction stages are carried out in a tube bundle reactor.
 17. A process as claimed in claim 5, wherein b=from 2 to 4, c=from 3 to 10, d=from 0.02 to 2, and e=from 0 to
 5. 18. A process as claimed in claim 1, wherein said interrupting the gas phase partial oxidation is carried out at least once within 7500 operating hours.
 19. A process as claimed in claim 1, wherein said interrupting the gas phase partial oxidation is carried out at least once within 7000 operating hours.
 20. A process as claimed in claim 1, wherein said interrupting the gas phase partial oxidation is carried out at least once within 6000 operating hours.
 21. A process as claimed in claim 1, wherein said interrupting the gas phase partial oxidation is carried out at least once within 5500 operating hours.
 22. A process as claimed in claim 1, wherein said interrupting the gas phase partial oxidation is carried out at least once within 5000 operating hours.
 23. A process as claimed in claim 1, wherein said interrupting the gas phase partial oxidation is carried out at least once within 4000 operating hours.
 24. A process as claimed in claim 1, wherein said interrupting the gas phase partial oxidation is carried out at least once within 3000 operating hours.
 25. A process as claimed in claim 1, wherein said interrupting the gas phase partial oxidation is carried out at least once within 2000 operating hours.
 26. A process as claimed in claim 1, wherein said interrupting the gas phase partial oxidation is carried out at least once within 1500 operating hours.
 27. A process as claimed in claim 1, wherein said interrupting the gas phase partial oxidation is carried out at least once within 1000 operating hours.
 28. A process as claimed in claim 1, wherein said interrupting the gas phase partial oxidation is carried out at least once within 500 operating hours.
 29. A process as claimed in claim 1, wherein said interrupting the gas phase partial oxidation is carried out at least once before the temperature increase of the fixed catalyst bed 2 is permanently ≧3° C.
 30. A process as claimed in claim 1, wherein said interrupting the gas phase partial oxidation is carried out at least once before the temperature increase of the fixed catalyst bed 2 is permanently ≧2° C.
 31. A process as claimed in claim 1, wherein the temperature increase of the fixed catalyst bed 2 is permanently ≧0.1° C. before said interrupting the gas phase partial oxidation is carried out at least once.
 32. A process as claimed in claim 1, wherein the temperature increase of the fixed catalyst bed 2 is permanently ≧0.2° C. before said interrupting the gas phase partial oxidation is carried out at least once. 